The invention belongs to the field of catalyst manufacturing technology, and provides a catalyst for hydrogenation of nickel to hydroxy - valeraldehyde to prepare new p - glycol. The composition of nickel oxide, alumina, silica and active additives; the composition of the quality of nickel oxide, alumina and silica is 25%~35%, 45%~60%, and 14%~20% active agent 0.1%~2.0%, which improves the selectivity of the catalyst to the new amyl glycol. The catalyst of the invention is prepared by co precipitation method. The conversion rate of new amyl glycol is high, the selectivity is good, the reaction condition is mild, the conversion of hydroxyl new valaraldehyde can reach 99.93%, and the selectivity of new amyl glycol can reach 99.2%.
【技术实现步骤摘要】
镍系羟基新戊醛加氢制备新戊二醇的催化剂及制法
本专利技术属于催化剂
，具体涉及一种镍系羟基新戊醛加氢制备新戊二醇的催化剂。
技术介绍
新戊二醇主要用于生产饱和聚酯树脂，其衍生物广泛用于涂料、汽车、纺织、农药、塑料和石油等领域。以新戊二醇为原料生产的饱和聚酯树脂，其特有的新戊基结构使以之为原料制备的粉末涂料、高固组分涂料具有优异的流动性、柔韧性、化学稳定性、耐候性、抗氯性、热稳定性和耐紫外线照射等性能。随着人们环保意识的加强，粉末涂料、高固组分涂料等环保涂料迅速发展，致使新戊二醇应用市场日益扩大。此外，新戊二醇在不饱和聚酯树脂、医药、胶粘剂等领域也有应用，市场潜力很大。新戊二醇在工业上通常由歧化法缩合法两种方法制备。歧化法为，用强碱性催化剂，例如氢氧化钠、氢氧化钾或氢氧化钙，使异丁醛与甲醛缩合制得羟基新戊醛，再与甲醛在强碱作用下经坎氏反应生成新戊二醇。本反就的缺点是形成大量副产物甲酸盐，由于甲酸盐脱除困难。造成产品成本高、质量差。目前国际上已为缩合加氢工艺所代替。首先异丁醛和甲醛缩合制得羟基戊醛(HPA)，然后再加氢合成新戊二醇，该法具有产品收率高，副产物少，...
【技术保护点】
一种镍系羟基新戊醛加氢制新戊二醇的催化剂，其特征在于它由氧化镍、氧化铝、二氧化硅和活性助剂组成；氧化镍、氧化铝、二氧化硅质量组成分别为25%~35%、45%~60%、14%~20%，活性助剂0.1%~2.0%。
【技术特征摘要】
1.一种镍系羟基新戊醛加氢制新戊二醇的催化剂，其特征在于它由氧化镍、氧化铝、二氧化硅和活性助剂组成；氧化镍、氧化铝、二氧化硅质量组成分别为25%~35%、45%~60%、14%~20%，活性助剂0.1%~2.0%。2.如权利要求1所述催化剂，其特征在于催化剂活性助剂为Ce、La化合物中的一种或两种混合物，含量为0.1%~1%。3.如权利要求1或2所述催化剂，其特征在于制得的催化剂其BET比表面在120m2/g~210m2/g，孔容为0.16mL/g~0.35mL/g，平均孔半径为4nm~7nm。4.如权利要求1所述催化剂的制备方法，其特征在于采用共沉淀法进行催化剂制备，包括以下步骤...
【专利技术属性】
技术研发人员：孙中华，孙远龙，袁浩然，吴结华，张皓，张觅，
申请(专利权)人：中国石油化工股份有限公司，南化集团研究院，
类型：发明
国别省市：江苏,32