The present invention relates to a sealing material field, discloses a seal for automobile brake caliper wear, made from the following raw materials in weight portion: three EPDM 180~190, fluorine rubber, polyurethane resin, 130~140 16~18 11~13, titanium dioxide 3~5, polyimide melamine 0.7~0.9, urea 0.6~0.8, antistatic agent 0.3~0.5, defoaming agent 0.3~0.5; add three Yuan rubber, fluorine rubber, polyurethane resin and polyimide can obviously improve the seal tear resistance and tensile strength, adding titanium dioxide, melamine and urea, a wide range of raw materials, can significantly improve the seal and high-temperature wear resistance, delaying seal fatigue, avoid assembly leakage phenomenon to ensure the braking effect, brake caliper, ensure traffic safety.
【技术实现步骤摘要】
一种用于汽车制动钳的耐磨密封件
本专利技术主要涉及密封材料领域,尤其涉及一种用于汽车制动钳的耐磨密封件。
技术介绍
汽车制动钳是汽车的中药组成部分,汽车制动性能直接影响着汽车的行车安全,为保证人身和车辆的安全,必须为汽车配备十分可靠的制动系统,制动钳是盘式制动器的重要组成部分,制动钳密封性不良就会使汽车盘式制动器总成出现渗漏现象,从而降低制动力,使制动效果降低,严重的可能会造成交通事故,目前汽车制动钳使用的密封件耐磨性较低,容易出现微泄露,造成很大的安全隐患。
技术实现思路
为了弥补已有技术的缺陷,本专利技术的目的是提供一种用于汽车制动钳的耐磨密封件。一种用于汽车制动钳的耐磨密封件,由以下重量份的原料制成:三元乙丙橡胶180~190、全氟橡胶130~140、聚氨酯树脂16~18、聚酰亚胺11~13、钛白粉3~5、三聚氰胺0.7~0.9、尿素0.6~0.8、抗静电剂0.3~0.5、消泡剂0.3~0.5。优选的,用于汽车制动钳的耐磨密封件,由以下重量份的原料制成:三元乙丙橡胶185、全氟橡胶135、聚氨酯树脂17、聚酰亚胺12、钛白粉4、三聚氰胺0.8、尿素0.7、抗静电剂0.4、消泡剂0.4。所述的抗静电剂,为烷基磺酸钠、乙氧基化烷基胺、甘油-硬脂酸酯中的一种或几种的任意混合。所述的消泡剂,为苯乙醇油酸酯、二甲基硅油、聚硅氧烷中的一种或几种的任意混合。本专利技术的优点是:本专利技术提供的用于汽车制动钳的耐磨密封件,加入三元乙丙橡胶、全氟橡胶、聚氨酯树脂和聚酰亚胺能够明显提高密封件的抗撕裂和抗拉伸能力,加入钛白粉、三聚氰胺和尿素,原料广泛,能够显著提高密封件的耐高 ...
【技术保护点】
一种用于汽车制动钳的耐磨密封件,其特征在于,由以下重量份的原料制成:三元乙丙橡胶180~190、全氟橡胶130~140、聚氨酯树脂16~18、聚酰亚胺11~13、钛白粉3~5、三聚氰胺0.7~0.9、尿素0.6~0.8、抗静电剂0.3~0.5、消泡剂0.3~0.5。
【技术特征摘要】
1.一种用于汽车制动钳的耐磨密封件,其特征在于,由以下重量份的原料制成:三元乙丙橡胶180~190、全氟橡胶130~140、聚氨酯树脂16~18、聚酰亚胺11~13、钛白粉3~5、三聚氰胺0.7~0.9、尿素0.6~0.8、抗静电剂0.3~0.5、消泡剂0.3~0.5。2.根据权利要求1所述用于汽车油缸的耐高温密封件,其特征在于,由以下重量份的原料制成:三元乙丙橡胶185、全氟橡胶13...