一种合成SAPO‑34分子筛的方法技术
A method for the synthesis of SAPO molecular sieve 34
The invention provides a method for the synthesis of SAPO molecular sieve 34. With phosphate as phosphorus source, pseudoboehmite as aluminum source, silica sol as silicon source, three triethylamine as template, the first silicon source with phosphoric acid at 200 DEG C for preheating treatment for 3 to 4 hours, then the aluminum source, a mixture of phosphorus source and silicon source, organic template, water according to Al2O3: H3PO4: SiO2: R: H2O = 1: 2: (0.05 ~ 2): 3: (50 ~ 150) mole ratio made of synthetic gel, the gel at 200 DEG C and hydrothermal crystallization generated pressure 1 ~ 2 days, and then cooling, washing, separation, drying at room temperature, namely the product. By using the method of the invention has a more uniform distribution of SAPO silicon 34 molecular sieve product.
【技术实现步骤摘要】
一种合成SAPO-34分子筛的方法一、
本专利技术涉及一种合成SAPO-34分子筛的方法，具体讲是先将硅源用磷酸进行热处理，再以三乙胺为模板剂，合成硅分布均匀的的SAPO-34分子筛。二、
技术介绍
硅磷酸铝分子筛SAPO-34由PO4，AlO4和SiO4四面体构成三维骨架结构，SAPO-34分子筛具有中等强度的酸性中心，同时具有八元环微孔结构，在甲醇制低碳烯烃反应中表现出优异的催化性能。然而，在SAPO-34分子筛合成体系中，硅源的溶解性比较差，尤其当硅含量较高的时候，硅组份容易以不同大小“硅岛”的形式进入SAPO-34分子筛结构中，使得进入SAPO-34分子筛硅组份的含量、形态难以控制，造成了硅组份分布的不均匀，导致SAPO-34分子筛的催化性能不稳定。目前的研究是通过混合模板剂或者寻找新的模板剂的方法来调控硅在菱沸石笼中的形态(MicroporousandMesoporousMaterials，2008，114，416；MicroporousandMesoporousMaterials，2007，329，130)。三、
技术实现思路
本专利技术通过对硅源加以预处...
【技术保护点】
一种合成SAPO‑34分子筛的方法，其特征在于经过下述步骤：先将硅源用磷酸在200℃下预热处理3～4小时，再将铝源、磷源与硅源的混合物、有机模板剂和水混合均匀制成合成凝胶，成胶时的温度为15～35℃，然后将该合成凝胶在200℃和自生压力下水热晶化1～2天，然后冷却、水洗、分离、室温晾干，既得产品，其物料的摩尔比为Al2O3∶H3PO4∶SiO2∶R∶H2O＝1.0∶2.0∶(0.05～2.0)∶3.0∶(50～150)。
【技术特征摘要】
1.一种合成SAPO-34分子筛的方法，其特征在于经过下述步骤：先将硅源用磷酸在200℃下预热处理3～4小时，再将铝源、磷源与硅源的混合物、有机模板剂和水混合均匀制成合成凝胶，成胶时的温度为15～35℃，然后将该合成凝胶在200℃和自生压力下水热晶化1～2天，然后冷却、水洗、分离、室温晾干，既得产品，其物料的摩尔比为Al2O3∶H3PO4∶SiO2...
【专利技术属性】
技术研发人员：胡思，潘亚军，葛轶强，
申请(专利权)人：江苏有容催化技术研究所有限公司，
类型：发明
国别省市：江苏,32