The invention discloses a method for iron containing mesoporous molecular sieve catalyst for preparing azelaic acid, which comprises the following steps: unsaturated fatty acid, iron containing mesoporous molecular sieve catalyst, sixteen alkyl three methyl ammonium chloride after mixing, stirring and heating to 100 120 DEG C, adding hydrogen chloride solution after the reaction. Stirred tank mixing crystalline white powder precipitated solid obtained after drying azelaic acid. The advantages of the invention are that it is easy to separate from reactants, and is easy to recycle and recycle. There is not a large number of organic solvents, solid wastes and toxic gases discharged in the reaction, which is good for the environment.
【技术实现步骤摘要】
一种含铁介孔分子筛催化剂制备壬二酸的方法
本专利技术属于化工合成
，具体涉及一种利用不饱和脂肪酸以含铁介孔分子筛为催化剂制备壬二酸的方法。
技术介绍
壬二酸可以用作香料、润滑油、油剂的原料并用于醇酸树脂、漆和化工合成，大部分壬二酸用于生产壬二酸二辛酯(DOZ)增塑剂。DOZ用作电缆、薄膜、人造革等用的耐寒性增塑性，挥发性小，耐老化性。利用油酸等不饱和脂肪酸制备壬二酸是目前主要的合成方法，但缺点是固体催化剂的催化效果一般，不易与反应物分离。
技术实现思路
因此，本专利技术的目的在于提供一种利用不饱和脂肪酸制备壬二酸的方法，该方法以含铁介孔分子筛为催化剂，催化效果显著，易于与反应物分离。解决问题的方案如下：1、将不饱和脂肪酸、含铁介孔分子筛催化剂和十六烷基三甲基氯化铵以质量比为60：8：2进行混合，搅拌加热至100-120℃，以质量比为：1：25加入氯化氢溶液与混合液反应，反应结束后将混合液至于搅拌釜中进行搅拌，搅拌时间为6-8H，经搅拌釜搅拌结晶析出白色粉末，在干燥釜中干燥，干燥时间为3-4H，干燥温度为100-120℃，得到壬二酸固体。2、上述不饱和脂肪酸、含铁介孔分子筛催化剂和十六烷基三甲基氯化铵的质量比为60：8：2。3、上述氯化氢与混合液的质量比为：1：25。4、上述不饱和脂肪酸为油酸、亚麻酸及花生四烯酸。5、上述搅拌时间为6-8H，干燥温度为100-120℃，干燥时间为3-4H。本专利技术方法是以含铁介孔分子筛为催化剂，该催化剂催化效果显著，与反应物易于分离，便于回收、循环使用，反应中无大量有机溶剂、固体废弃物以及有毒气体排放，利于环境。具体实施...
【技术保护点】
一种含铁介孔分子筛催化剂制备壬二酸的方法，该方法包括如下步骤：将不饱和脂肪酸、含铁介孔分子筛催化剂、十六烷基三甲基氯化铵混合后，搅拌加热至100‑120℃，加入氯化氢溶液反应后，经搅拌釜搅拌结晶析出白色粉末，经干燥后得到壬二酸固体。
【技术特征摘要】
1.一种含铁介孔分子筛催化剂制备壬二酸的方法，该方法包括如下步骤：将不饱和脂肪酸、含铁介孔分子筛催化剂、十六烷基三甲基氯化铵混合后，搅拌加热至100-120℃，加入氯化氢溶液反应后，经搅拌釜搅拌结晶析出白色粉末，经干燥后得到壬二酸固体。2.根据权利要求1所述的一种含铁介孔分子筛催化剂制备壬二酸的方法，其特征是：所述不饱和脂肪酸、含铁介孔分子筛催化剂和十六烷基三甲基氯化铵的质量比为60：8...
【专利技术属性】
技术研发人员：胡思，潘亚军，周玉洁，
申请(专利权)人：江苏有容催化技术研究所有限公司，
类型：发明
国别省市：江苏,32