The invention discloses a method for preparing a core-shell silver / silver catalyst. The method comprises the following steps: 1 ~ 4G sixteen alkyl three methyl bromide 20mL dissolved in toluene, adding 4 ~ 5g 80 ~ 100 mesh sieve silver oxide powder, ultrasonic dispersion of 20 ~ 100min, adding 5 20mL water, 400 ~ 600 rpm by adding 0.5 ~ 1g borohydride sodium, continue stirring for 4 ~ 8min, precipitation separation, a core-shell silver / silver catalyst. As the silver precursor for the production of Ag and as a carrier to provide support of nano particle nucleation and growth of the active function, control of nanoparticles surfactants as templates for the growth of function, reducing agent is added to a mixture containing template support dual function micro reaction environment, reduction in the surface part, system kernel as the silver surface is core-shell type catalyst of silver, and silver / silver have synergistic effect, can better promote the catalytic effect.
【技术实现步骤摘要】
一种核壳型氧化银/银光催化剂的制备方法
本专利技术涉及环境污染控制新材料的开发,尤其涉及一种核壳型氧化银/银光催化剂的制备方法。
技术介绍
在生活污水、食品加工和造纸等工业废水中,含有碳水化合物、蛋白质、油脂、木质素等有机物质。这些物质以悬浮或溶解状态存在于污水中,可通过微生物的生物化学作用而分解。在其分解过程中需要消耗氧气,因而被称为耗氧污染物。这种污染物可造成水中溶解氧减少,影响鱼类和其他水生生物的生长。水中溶解氧耗尽后,有机物进行厌氧分解,产生硫化氢、氨和硫醇等难闻气味,使水质恶化。随着生产的发展,来自工农业生产中产生的毒害有机污染物严重威胁着环境和人类的健康,寻求一种新型高效的环境治理技术具有重要的意义。光催化技术因其节能、高效、污染物降解彻底、无二次污染优点,目前已成为一种具有重要应用前景的新兴环境治理技术。近年来,新型高效的可见光光催化剂的研制成为光催化技术中的一个重要研究内容。氧化银(Ag2O)是一种p型半导体,其带隙能为1.46eV,在可见光区内有较强的光吸收,是一种高活性和高选择性的窄带隙光催化剂。但是氧化银在光照后导带产生的光电子会将Ag+还原成Agn单质簇,而价带的空穴会氧化晶格中的O2-释放O2,所以会产生催化剂本身的光腐蚀现象。同时氧化银纳米粒子中的银离子将和残留的一部分氧结合,其晶格将发生重构,从而产生各种类似分子的光解发光中心。光解中心的出现将在氧化银的禁带中引入若干缺陷能级,从而使得氧化银纳米粒子利用光子效率提高。在光腐蚀的过程中,当单质银和氧化银的相对含量达到一定值时,后续会保持稳定性。
技术实现思路
本专利技术的目的是为克服 ...
【技术保护点】
一种核壳型氧化银/银光催化剂的制备方法,其特征是依次包括如下步骤:将1~4g十六烷基三甲基溴化铵溶解到20mL甲苯中,加入4~5g过80~100目筛的氧化银粉末,超声分散20~100min,加入5~20mL水,在400~600转/分钟的转速下加入0.5~1g硼氢化钠,继续搅拌4~8min,沉淀分离,得到一种核壳型氧化银/银光催化剂。
【技术特征摘要】
1.一种核壳型氧化银/银光催化剂的制备方法,其特征是依次包括如下步骤:将1~4g十六烷基三甲基溴化铵溶解到20mL甲苯中,加入4~5g过80~100目筛的氧化银粉末,超...