The invention belongs to the field of polymer processing technology, particularly relates to a method for preparing polyether ketone ketone powder. The polyetherketoneketone coarse powder and two phenyl sulfone granulation in double screw extruder, obtained PEKK particles containing two benzene sulfone; then grinding, and then pulverized by jet mill, finally using acetone and water purification product. The present invention due to the addition of two phenyl sulfone in polyetherketoneketone, greatly reduced the PEKK toughness to brittleness increases, ultrafine powder does not need more complex process to produce polyether ketone ketone; polyether ketone ketone powder formed by this method has the advantages of narrow size distribution and small particle size, can be dispersed to very easy to paint liquid.
【技术实现步骤摘要】
聚醚酮酮细粉的制备方法
本专利技术属于高分子加工
，具体涉及一种聚醚酮酮细粉的制备方法。
技术介绍
聚醚酮酮(PAEK)是一种具有优异性能的特种工程塑料，其具有优异的耐磨性、机械性能、耐化学腐蚀、耐高温等性能。目前已被广泛的应用到航空航天、电子通讯、石油化工、以及医疗卫生等领域。聚醚酮酮属于热塑性树脂，其作为涂层材料来说具有与基材的附着力好，耐磨性好，是用作涂层基体材料的理想聚合物之一。目前已经有工业化的聚醚醚酮涂层和聚醚酮酮涂层应用在汽车和工业部件、家用炊具和食品加工行业。由于聚醚酮酮具有较高的韧性，导致其很难粉碎成较细的粒子，尤其是当聚醚酮酮的分子量比较高时，即便是采用液氮进行冷却的气流磨进行粉碎的话，也很难将其粉碎至较小粒径，较难制备超细粒径的聚醚酮酮粉末。
技术实现思路
针对现有技术的不足，本专利技术的目的是提供一种聚醚酮酮细粉的制备方法，不需要较为复杂的工艺就能生产聚醚酮酮的超细微粉，粒径分布窄、粒径小，能够很容易的分散至液体涂料中去。。本专利技术所述的聚醚酮酮细粉的制备方法，将聚醚酮酮粗粉与二苯砜在双螺杆挤出机中进行造粒，得到含二苯砜的聚醚酮酮粒子；...
【技术保护点】
一种聚醚酮酮细粉的制备方法，其特征在于：将聚醚酮酮粗粉与二苯砜在双螺杆挤出机中进行造粒，得到含二苯砜的聚醚酮酮粒子；再磨碎，然后用气流粉碎机进行粉碎，最后分别用丙酮和水进行纯化，得到产品。
【技术特征摘要】
1.一种聚醚酮酮细粉的制备方法，其特征在于：将聚醚酮酮粗粉与二苯砜在双螺杆挤出机中进行造粒，得到含二苯砜的聚醚酮酮粒子；再磨碎，然后用气流粉碎机进行粉碎，最后分别用丙酮和水进行纯化，得到产品。2.根据权利要求1所述的聚醚酮酮细粉的制备方法，其特征在于：步骤如下：(1)将聚醚酮酮粗粉放入双螺杆挤出机的主喂料机中，侧喂料机中放入二苯砜单体，然后进行造粒，得到含二苯砜的聚醚酮酮粒子；(2)将含二苯砜的聚醚酮酮粒子用盘磨机进行磨碎，制得含二苯砜的聚醚酮酮粗粉；(3)将含二苯砜的聚醚酮酮粗粉用气流粉碎机进行粉碎，制成含二苯砜的聚醚酮酮细粉；(4)将步骤(3)制备的含二苯砜的聚醚酮酮细粉分别用丙酮和水进行纯化，干燥...
【专利技术属性】
技术研发人员：李光辉，李云龙，王帅坡，戴士园，黄桂青，兰燕，张际亮，张泰铭，
申请(专利权)人：山东凯盛新材料股份有限公司，
类型：发明
国别省市：山东,37