The invention discloses a method for preparing a dehydrogenation catalyst, are as follows: (1) the chloroplatinic acid, sodium nitrite and water mixed evenly by impregnating solution; (2) dipping the boiling and mixing, and then cooled to room temperature; (3) in step (2) by immersion waterlogging liquid dipping treatment of inorganic oxide carrier, by impregnation process, then drying and roasting, get dehydrogenation catalyst. The method does not need hydrothermal dechlorination, and avoids the accumulation and growth of Pt particles. The preparation method of the catalyst is simplified, the energy consumption is reduced, and the production cost is saved.
【技术实现步骤摘要】
一种脱氢催化剂的制备方法
本专利技术涉及一种脱氢催化剂的制备方法，具体地涉及一种无须水热脱氯的脱氢催化剂的制备方法。
技术介绍
北美页岩气的开发已经导致天然气价格相对于原油价格的大幅下降，而页岩气中大量的凝析液（NGLs）产量也迅速增长。页岩气凝析液中富含乙烷、丙烷、丁烷等低碳烷烃，乙烷可以作为裂解原料生产乙烯，因此仅靠FCC技术已经不能丙烯快速增长的需求。将天然气（常规天然气、页岩气、煤层气、可燃冰等）中的低碳烷烃脱氢制取低碳烯烃是解决这一问题的有效途径。而且随着石油资源的日益匮乏，丙烯的生产已从单纯依赖石油为原料向原料来源多样化的技术路线转变，也逐渐成为一种趋势。近几年来，丙烷脱氢生产丙烯的技术取得了较大发展，特别是丙烷脱氢(PDH)制丙烯的技术发展较快，已经成为第三大丙烯生产方法。目前，世界上低碳烷烃脱氢专利技术包括：UOP公司的Oleflex工艺，ABB鲁姆斯公司的Catofin工艺，康菲(Uhde)公司的Star工艺，Snamprogetti/Yarsintz公司的FBD-4工艺，林德/巴斯夫公司的PDH工艺等。在已经建设的装置中，前苏联大多数采用FBD...
【技术保护点】
一种脱氢催化剂的制备方法，其特征在于包括如下内容：（1）将氯铂酸、亚硝酸钠和水混合均匀得到浸渍液；（2）将浸渍液加热煮沸，并搅拌，然后冷却至室温；（3）用步骤（2）得到的浸渍液浸渍处理无机氧化物载体，然后干燥、焙烧，得到脱氢催化剂。
【技术特征摘要】
1.一种脱氢催化剂的制备方法，其特征在于包括如下内容：（1）将氯铂酸、亚硝酸钠和水混合均匀得到浸渍液；（2）将浸渍液加热煮沸，并搅拌，然后冷却至室温；（3）用步骤（2）得到的浸渍液浸渍处理无机氧化物载体，然后干燥、焙烧，得到脱氢催化剂。2.按照权利要求1所述的方法，其特征在于：步骤（1）所述的浸渍液中氯铂酸、亚硝酸钠和水的摩尔比为：1:4~10:1000~30000。3.按照权利要求1所述的方法，其特征在于：步骤（1）所述的浸渍液中氯铂酸、亚硝酸钠和水的摩尔比为：1:4.5~6:2000~20000。4.按照权利要求1所述的方法，其特征在于：步骤（2）所述煮沸的温度为90~110℃，煮沸时间为10~60分钟。5.按照权利要求1所述的方法，其特征在于：步骤（2）所述的搅拌速度为40~120转/分钟。6.按照权利要求1所述的方法，其特征在于：步骤（3）所述浸渍液与无机氧化...
【专利技术属性】
技术研发人员：王振宇，郑步梅，张淑梅，
申请(专利权)人：中国石油化工股份有限公司大连石油化工研究院，中国石油化工股份有限公司，
类型：发明
国别省市：辽宁,21
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。