The invention discloses a method for preparing phenolic resin, the method comprises the following steps: (1) benzene and formaldehyde cresol molar of 1.1-1.8:1 added to the reactor, mixing evenly heated to 60-90 DEG C; (2) in the mixture adding acidic catalyst; (3) in the mixture the mixture of modified agent, toughening agent, rare earth metal in an arbitrary, arbitrary two or three; (4) thermal condensation reaction for 1-4 hours; (5) adding emulsifier in reactor and stirring, insulation and emulsified reaction for 0.5-1.5 hours; (6) heating to 100-110 deg.c for dehydration 0.5-1 h; (7) cooling material to 50 DEG C after discharge of phenolic resin. The preparation process of the invention is simple, the operation is easy, the product has the advantages of high carbon content, good toughness, high yield, low comprehensive cost, low energy consumption ratio, waste gas, waste water and waste material recycling and energy saving and environmental protection.
【技术实现步骤摘要】
本专利技术涉及高分子聚合物
，具体的说是。
技术介绍
酚醛树脂是酚类和醛类在催化剂存在的条件下反应形成的树脂的统称。采用传统的酚醛树脂制备方法制备酚醛树脂，在生产过程中，产生大量的含有高浓度的酚、醛和树脂等有机物的工业废水，具有高有机物浓度、高毒性的特点。这种工业废水的处理程序复杂， 效果也不理想。给酚醛树脂的生产企业带来很大压力，严重制约着企业的发展。
技术实现思路
本专利技术的目的是针对现有技术的缺陷，提供一种含碳量高、韧性好、可废水回用的酚醛树脂制备方法。本专利技术的目的是通过以下技术方案解决的，所述的制备方法按下述步骤进行(1)将苯甲酚和甲醛按摩尔比1.1-1. 8 1加入反应釜中，两者搅拌混合均勻后加热升温到 60-90 0C ；(2)在混合物中滴加酸性催化剂；(3)在混合物中加入改性剂、增韧剂、稀土金属中的任意一种，或其中的任意两种，或三者的混合物；(4)保温进行缩合反应1-4小时；(5)在反应釜中加入乳化剂并搅拌，保温进行乳化反应0.5-1. 5小时；(6)升温到100-110°C进行脱水0.5-1小时；(7)冷却降温到50°C以下后放料得酚...
【技术保护点】
１．一种酚醛树脂的制备方法，其特征在于所述的制备方法按下述步骤进行：（１）将苯甲酚和甲醛按摩尔比１．１－１．８：１加入反应釜中，两者搅拌混合均匀后加热升温到６０－９０℃；（２）在混合物中滴加酸性催化剂；（３）在混合物中加入改性剂、增韧剂、稀土金属中的任意一种，或其中的任意两种，或三者的混合物；（４）保温进行缩合反应１－４小时；（５）在反应釜中加入乳化剂并搅拌均匀，保温进行乳化反应０．５－１．５小时；（６）升温到１００－１１０℃进行脱水０．５－１小时；（７）冷却降温到５０℃以下后放料得酚醛树脂。
【技术特征摘要】
【专利技术属性】
技术研发人员：张吉太，刘明秋，邹开良，
申请(专利权)人：江苏国正新材料科技有限公司，
类型：发明
国别省市：32