The present invention relates to the field of polymer synthesis and modification technology, in particular to a preparation method of cardanol modified phenolic resin, which comprises the following steps: 1) and cardanol aldehyde under acidic conditions, dehydration after A components; 2) phenol and aldehyde reaction under acidic conditions after dehydration of B component; 3) of A were divided into B group and acid, reaction after dehydration by cardanol modified phenol formaldehyde resin. The beneficial effect of the invention is that the phenol formaldehyde modified phenolic resin prepared by the method of the invention has the advantages of better toughness and heat resistance, good processability and low production cost.
【技术实现步骤摘要】
一种腰果酚改性的酚醛树脂的制备方法
本专利技术涉及高分子合成与改性
，具体说是一种腰果酚改性的酚醛树脂的制备方法。
技术介绍
随着工业发展水平的不断提高，对酚醛树脂性能的要求也越来越高，国内外酚醛树脂行业和塑料行业对酚醛树脂的改性进行了大量的研究工作，高韧性和耐热性是酚醛树脂的发展方向。从缩聚机理及酚醛树脂的反应机理来看，改性途径主要有：(1)直接封锁酚烃基；(2)引进其他组分，通过其他组分分割酚烃基，从而达到改变固化速度、降低吸水性、提高性能的目的；(3)引进具有柔性基团的物质，调节树脂的刚性。生产酚醛树脂的主要原料苯酚与甲醛是典型的石油化工产品，近年来价格飞涨。随着石油资源的短缺，其前景更不乐观。因此，采用基于可再生资源的廉价的化工原料替代或部分替代石油化工原料已引起人们的重视。腰果壳油(cashewnutshellliquid，CNSL)是腰果加工过程中的农业副产物，可以从腰果壳中萃取得到，其资源丰富、价格低廉、性能独特，主要成分为腰果酚，加固提炼，腰果酚的含量可达到95％以上。从其主要组分的结构可以看出，它是侧基带有不饱和脂肪链的酚类化合物，因此可以...
【技术保护点】
腰果酚改性的酚醛树脂的制备方法，其特征在于，包括如下步骤：1)将腰果酚与醛在酸性条件下反应，脱水后得到A组分；2)将酚与醛在酸性条件下反应，脱水后得到B组分；3)将A组分和酸加入B组分，反应后脱水得到腰果酚改性酚醛树脂。
【技术特征摘要】
1.腰果酚改性的酚醛树脂的制备方法，其特征在于，包括如下步骤：1)将腰果酚与醛在酸性条件下反应，脱水后得到A组分；2)将酚与醛在酸性条件下反应，脱水后得到B组分；3)将A组分和酸加入B组分，反应后脱水得到腰果酚改性酚醛树脂。2.根据权利要求1所述的腰果酚改性酚醛树脂的制备方法，其特征在于，具体包括如下步骤：1)将腰果酚与醛加入反应釜中，搅拌均匀，用酸调节反应液的pH为2-5，升温至80-120℃，反应1-6h，脱水后得到A组分；2)将酚与醛加入另一应釜中，搅拌均匀，用酸调节pH为2-5，在温度为70-100℃下反应1-5h，脱水后得到B组分；3)将A组分和酸加入B组分，回流反应1-5h，脱水得到腰果酚改性酚醛树脂。3.根据权利要求2所述的腰果酚改性的酚醛树脂的制备方法，其特征在于：所述的腰果酚的添加量为酚质量的...
【专利技术属性】
技术研发人员：黄世俊，罗建峰，艾生儿，翟苏宇，王堂明，张振伟，
申请(专利权)人：沙县宏盛塑料有限公司，
类型：发明
国别省市：福建,35
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。