一种聚酰胺改性酚醛树脂的合成制造技术

本发明专利技术涉及一种聚酰胺改性酚醛树脂的合成，技术方案如下：准确称取聚酰胺改性酚醛树脂100‑150g、正己醇6‑8g、阻聚剂对羟基苯甲醚0.1g、催化剂钛酸丁酯0.01g，加入到带有温度计的三口烧瓶中，升温至65度，开始滴加22g二异氰酸酯IPDI，将温度控制在70‑75度，反应3‑5h。用红外光谱仪分析NCO基团的含量，待NCO的峰完全消失时，停止加热反应，得到聚酰胺改性酚醛树脂。

Synthesis of a kind of polyamide modified phenolic resin

The present invention relates to the synthesis of a polyamide modified phenolic resin, the technical scheme is as follows: weigh polyamide modified phenolic resin 100 150g, hexanol 6 8g inhibitor, 4-methoxyphenol 0.1g catalyst, butyl titanate 0.01g, added to the three flasks with a thermometer, the temperature to 65 degrees start, dropping 22G diisocyanate IPDI temperature control in 70 75 degrees, 3 5h reaction. The content of NCO group was analyzed by infrared spectrometer. When the peak of NCO was completely disappeared, the reaction of heating was stopped and polyamide modified phenolic resin was obtained.

【技术实现步骤摘要】
一种聚酰胺改性酚醛树脂的合成
本专利技术涉及一种聚酰胺改性酚醛树脂的合成，属于合成化学领域。
技术介绍
电容式触摸屏的表面保护层和导电层大多采用玻璃基材，其折射率在1.52左右，所以要求其粘接材料的折射率尽可能与其相等，可以大量减少光线在界面间的折射损失，提高平板显示器在强光环境中的对比度和清晰度。同时在紫外线照射、湿热老化、冷热冲击等苛刻条件下，光学透明胶需要保持高透光率、低黄变等重要指标的稳定。而传统的液态光学透明胶的折射率一般在1.50以下，较低的折射率影响平板显示器在强光环境中的对比度和清晰度；因此本专利技术就提供了一种更折射率的光学树脂，折射率在1.52-1.54，具有更好的耐黄变性，用来制作更高端的液态光学透明胶，具有很好的应用价值。
技术实现思路
本专利技术所要解决的技术问题是提供一种聚酰胺改性酚醛树脂的合成，该树脂用于光学透明胶。本专利技术解决上述技术技术方案如下：准确称取聚酰胺改性酚醛树脂100-150g、正己醇6-8g、阻聚剂对羟基苯甲醚0.1g、催化剂钛酸丁酯0.01g，加入到带有温度计的三口烧瓶中，升温至65度，开始滴加22g二异氰酸酯IPDI，将温度控制在70-本文档来自技高网...

【技术保护点】
一种聚酰胺改性酚醛树脂的合成，其特征在于，包括

【技术特征摘要】
1.一种聚酰胺改性酚醛树脂的合成，其特征在于，包括：准确称取聚酰胺改性酚醛树脂100-150g、正己醇6-8g、阻聚剂对羟基苯甲醚0.1g、催化剂钛酸丁酯0.01g，加入到带有温度计的三口烧瓶中，升温至65度，开始滴加22g二异氰酸酯IPDI，将温度控制在70-75度，反应3-5h；用红外...