一种含氮环氧树脂固化物的制备方法技术

本发明专利技术公开了一种含氮环氧树脂固化物的制备方法，包括以下步骤：（1）搅拌条件下，将E-51型环氧树脂、双酚A、三聚氰酸三缩水甘油胺、三苯基磷、固化剂加入反应器进行反应，得到熔融的环氧树脂基体；（2）将熔融的环氧树脂基体倒入成型模中进行升温固化反应，冷却后即得到所述的含氮环氧树脂固化物。该方法未使用有机溶剂，彻底解决了环氧固化物中溶剂残留的问题；在固化物中引入了通用的E-51型环氧树脂，既降低了环氧基体的粘度，又有利于操作，同时又将三聚氰酸三缩水甘油胺中的三嗪环引入环氧树脂链中，达到了阻燃的效果。

Method for preparing nitrogen containing epoxy resin curing agent

The invention discloses a nitrogen containing epoxy resin, preparation method, which comprises the following steps: (1) under the condition of stirring, E-51 type epoxy resin, bisphenol A, cyanuric acid three, three phenyl glycidyl amine and phosphorus curing agent into the reaction, obtained epoxy resin matrix melt; (2) the epoxy resin melt into the mold in the temperature of curing reaction, nitrogen containing epoxy resin after cooling to obtain the. The method does not use organic solvent, completely solve the residual solvent in the cured epoxy; E-51 type epoxy resin curing is introduced in general, not only reduces the viscosity of the epoxy matrix, but also conducive to the operation, and three cyanuric acid has shrunk three triazine ring in the glycerol amine epoxy chain the flame retardant effect, achieve.

【技术实现步骤摘要】

本专利技术涉及。
技术介绍
世界许多国家或地区(特别是欧洲)己制定、颁布了众多有关限制或禁用含卤系阻燃基板材料的法规，卤系阻燃高分子材料在欧洲未能获得绿色环保标志。世界一些著名电子产品厂家己开始使用不含卤素的基材。根据世界有关机构最近分析，在2005—2010 年，由于包括“欧洲两个指令”(WEEE & RoHS，2006年7月1日生效)在内的各项有关禁止使有害含卤材料法令的实施，促使世界的无卤化基板材料用量迅速增加到占总用量的50% 一 80%。为了应对欧盟指令，世界各国都把绿色型覆铜板的开发作为研讨的焦点之一。用来代替溴化环氧树脂的新型阻燃环氧树脂的应用需求有着巨大的潜力。目前绿色环保型阻燃环氧树脂主要包括含膦、含氮、含硅树脂。含磷环氧树脂具有较高的阻燃效率，但耐湿热性能低下，部分含磷阻燃剂水溶性强，其制品使用结束丢弃后，磷易被溶出，也可能对环境造成污染。含硅环氧树脂耐热、防潮，具有较好的电气性能、粘合性和机械强度，但玻璃化转变温度普遍较低，并且与多数环氧树脂相容性不好。含氮环氧树脂作为一种新型的阻燃环氧树脂，具有较高的热分解温度和阻燃效率，是目前取代含溴环氧树脂的主本文档来自技高网...

【技术保护点】
１．一种含氮环氧树脂固化物的制备方法，其特征在于：该方法包括以下步骤：（１）搅拌条件下，将Ｅ－５１型环氧树脂、双酚Ａ、三聚氰酸三缩水甘油胺、三苯基磷、固化剂加入反应器，在温度１００－１５０℃条件下反应１－３小时，得到熔融的环氧树脂基体；（２）将熔融的环氧树脂基体倒入成型模中，在温度１５０－２００℃条件下，固化反应１－１０小时，冷却后即得到所述的含氮环氧树脂固化物。

【技术特征摘要】

【专利技术属性】
技术研发人员：赵庭栋，闫晓红，魏军波，李善清，徐文辉，马西忠，刘杰，
申请(专利权)人：山东天一化学股份有限公司，
类型：发明
国别省市：37