The present invention discloses a method for preparing alumina carrier with concentrated pore distribution. Alumina monohydrate in acidic aqueous solution adhesive containing at least one organic acid solution, then the aqueous alkaline solution treatment of granular solids acidification, the pH value reached more than 7.5, then, produced by kneading and extruding process heat, the temperature of above 70 DEG C extrusion. In the preparation process of the present invention, no strong acid such as nitric acid or hydrochloric acid is used as a gum solvent. Thereby, the destruction of the pore structure of the carrier due to the use of the substance is eliminated, and the pollution of the nitride, chloride and the like produced by the carrier roasting process is eliminated.
【技术实现步骤摘要】
本专利技术涉及具有集中孔分布的大孔容氧化铝载体的制备方法。众所周知，性质优良的催化剂载体是获取高性能负载型加氢处理催化剂的关键。对于渣油加氢脱金属催化剂而言，具有大孔容、适宜的孔径和孔分布是催化剂保持高活性和长寿命的重要保证。中国专利申请95194329．4公开了一种氧化铝载体的制备方法。制备氧化铝载体的主要步骤是，将固体氧化铝一水合物用硝酸或其等效物如盐酸、氢氟酸和氢溴酸的酸性水溶液混合至PH值达到约3．0-4．5；然后，将氨碱水溶液混入酸处理过的粒状固体，至少部分地中和酸处理过的粒状固体氧化铝一水合物，氨碱水溶液含碱量通常每当量酸为约0．9-约1．1当量氨碱；将经中和或部分中和的固体成形并干燥；在温度至少871℃下煅烧已成形的固体。按上述公开方法制备的氧化铝载体存在的问题是，硝酸、盐酸等无机盐的酸强度很强，很容易对氧化铝一水化合物的孔结构构成破坏，由此导致孔直径小于14nm的小孔增多。该方法的另一问题是载体在焙烧过程中产生的氮化物、氯化物、氟化物或溴化物等将对环境产生严重的污染。本专利技术的目的是提供一种能够有效促进氧化铝载体孔分布集中及孔容增大的无环境...
【技术保护点】
一种具有集中孔分布的氧化铝载体的制备方法，其步骤为： １）将氧化铝一水合物用含有一种或多种有机酸的弱酸性水溶液胶溶； ２）再用含有氨水和一种或多种可完全挥发的铵盐的碱性水溶液处理酸化过的粒状固体，使ＰＨ值达到７．５以上；碱性水溶液中氨的碱当量数是酸性水溶液中有机酸当量数的１．０５倍以上，铵盐重量是干基氧化铝投料重量的０．２－２．２ｍ％； ３）利用捏合和挤条过程中产生的热量，在７０℃以上的温度下挤条； ４）经干燥后，在温度至少９３０℃下焙烧处理后得氧化铝载体。
【技术特征摘要】
1．一种具有集中孔分布的氧化铝载体的制备方法，其步骤为1)将氧化铝一水合物用含有一种或多种有机酸的弱酸性水溶液胶溶；2)再用含有氨水和一种或多种可完全挥发的铵盐的碱性水溶液处理酸化过的粒状固体，使PH值达到7．5以上；碱性水溶液中氨的碱当量数是酸性水溶液中有机酸当量数的1．05倍以上，铵盐重量是干基氧化铝投料重量的0．2-2．2m％；3)利用捏合和挤条过程中产生的热量，在70℃以上的温度下挤条；4)经干燥后，在温度至少930℃下焙烧处理后得氧化铝载体。2．按照权利要求1所述的制备方法，其中步骤1)中所说的有机酸是甲酸、乙酸、丙酸、柠檬酸、酒石酸或水杨酸。3．按照权利要...
【专利技术属性】
技术研发人员：赵愉生，刘喜来，王志武，方维平，陈晓静，杨刚，
申请(专利权)人：中国石油化工集团公司，中国石油化工集团公司抚顺石油化工研究院，
类型：发明
国别省市：11[中国|北京]