一种可溶性敷料及其制备方法技术
A kind of soluble dressings and their preparation methods
The invention discloses a medical antiseptic hydrogel dressing and a preparation method. Preparation of hydrogels prepared by the method of the invention, the preparation process to add a thickener, without affecting the dressing function, is conducive to form the dressing; hydrogel dressing preparation method of the invention has excellent bacterial isolation effect, can effectively resist the invasion of foreign bacteria, prevent the wound two times of infection, promote wound healing; preparation of hydrogels prepared by the method of the invention can be dissolved in an appropriate solvent, the replacement is very convenient, without mechanical tear, tear is not healing wounds, relieve the pain of patients.
【技术实现步骤摘要】
一种可溶性敷料及其制备方法
本专利技术属于医用制品
，具体涉及一种医用抗菌可溶解的水凝胶敷料及其制备方法。
技术介绍
传统的伤口敷料是由天然植物纤维或动物毛类物质构成，如纱布、棉垫、羊毛、各类油纱布等，这类敷料只是暂时性的覆盖材料，都需在一定的时间内加以更换。然而，这些伤口敷料在更换时容易发生与伤口相互沾黏之情况，因此在撕除敷料的同时有可能一并撕开新生的上皮细胞或已逐渐愈合的伤口，导致使用者疼痛难耐，且不利于伤口愈合。水凝胶医用敷料是近年来发展起来的一种新型创伤敷料，与目前临床上所用的传统的纱布敷料等相比，水凝胶敷料透气保湿，不仅能够缩短伤口愈合的时间，减轻患者的疼痛，由于敷料透明还能方便观察伤口的愈合情况，因而得到各国的普遍重视。但该类敷料对细菌的隔离作用有限，易污染需勤换敷料和药物。对于伤口较深、面积较大的患者来说，频繁地更换敷料和清创必然会造成新生上皮组织的破坏，不利于伤口愈合。同时，由于水凝胶敷料在聚合反应之前为水溶液状态，粘度极低，需在专门的容器中才能进行聚合反应并成型，制作过程复杂，无法实现快速大量生产，且不利于成型适合异形创面的敷料，生产效率较...
【技术保护点】
一种可溶性水凝胶敷料的制备方法，其特征在于，包括如下步骤：（1）室温下，将水溶性烯类单体、可溶性水凝胶用交联剂、水、引发剂，增稠剂、抗菌剂混合，搅拌分散均匀，制备成混合溶液；所述的可溶性水凝胶用交联剂的分子结构如下所示：
【技术特征摘要】
1.一种可溶性水凝胶敷料的制备方法，其特征在于，包括如下步骤：（1）室温下，将水溶性烯类单体、可溶性水凝胶用交联剂、水、引发剂，增稠剂、抗菌剂混合，搅拌分散均匀，制备成混合溶液；所述的可溶性水凝胶用交联剂的分子结构如下所示：式中，R1为氢或甲基；R为—(CH2CH2)n—，或—(CH2)y(CH2CH2O)x(CH2)y—，其中，n为1~10，x为1~5000，y为0~10；（2）将混合溶液均匀涂布于基材上，形成胶体涂层；使胶体涂层在引发剂的作用下发生交联反应，在基材上形成水凝胶层；（3）将基材上形成的水凝胶层剥离下来，得到可溶性水凝胶敷料。2.根据权利要求1所述的一种可溶性水凝胶敷料的制备方法，其特征在于：在所述步骤（1）中，水溶性烯类单体、可溶性水凝胶用交联剂、水、引发剂，增稠剂和抗菌剂的质量比为1：（0.01~2）：（1~100）：（0.0001~0.1）：（0.001~0.1）：（0.001~0.1）。3.根据权利要求1所述的一种可溶性水凝胶...