The invention relates to a method for preparing Nanotube Titanic Acid embedded in transition metal and its oxide, belonging to the technical field of Nanotube Titanic Acid preparation. Includes the following steps: (1) the transition metal salt solution steps of titanate nanotubes concentration and 0.12000mg / ml in 0.020.1MPa under vacuum, the quality of titanate nanotubes and transition metal salts ratio (0.120000): 1; (2) the mixture placed under normal pressure reaction 0.172 hours; purification treatment; ((3) 4) transition metal salt conversion reaction steps, the steps in the purification of the product in 501000 C air calcination 0.572 hours, or 501000 C calcined in hydrogen atmosphere 0.572 hours, or by visible light and ultraviolet light irradiation 0.272 hours. The invention provides a method for preparing Nanotube Titanic Acid with embedded transition metal and its oxide, which has simple method and mild condition.
【技术实现步骤摘要】
本专利技术属于纳米管钛酸制备
，特别涉及一种。
技术介绍
纳米管作为一种新型纳米级材料正在得到广泛的关注，填充金属及其氧化物的纳米管具有很多工业用途，如在大规模集成电路中作为同轴电缆或化工生产中作为催化剂等。填充过渡金属及其氧化物的纳米管钛酸的制备和应用方面的研究，将会得到令人惊叹的效果。由于纳米管钛酸内径较小，仅有2-8纳米，在纳米管钛酸中填充过渡金属及其氧化物有一定困难。
技术实现思路
本专利技术目的在于提供一种。为达上述目的，本专利技术采用如下技术方案，包括如下步骤(1)纳米管钛酸在0.02-0.1Mpa真空度下与0.1-2000mg/ml浓度的过渡金属盐溶液混合步骤，纳米管钛酸与过渡金属盐的质量比为(0.1-20000)∶1；(2)上述混合液在常压下放置反应0.1-72小时；(3)净化处理；(4)过渡金属盐转化反应步骤，该步骤中，把净化处理所得产物在50-1000℃空气中煅烧0.5-72小时，或者在50-1000℃氢气氛中煅烧0.5-72小时，或者用可见光、紫外光照射0.1-72小时。过渡金属盐溶液包括过渡金属盐与水溶剂、乙醇溶剂、乙醚溶剂、丙酮溶剂...
【技术保护点】
嵌入过渡金属及其氧化物的纳米管钛酸的制备方法，其特征在于，包括如下步骤：（１）纳米管钛酸在０．０２－０．１Ｍｐａ真空度下与０．１－２０００ｍｇ／ｍｌ浓度的过渡金属盐溶液混合步骤，纳米管钛酸与过渡金属盐的质量比为（０．１－２００００）∶１；（２）上述混合液在常压下放置反应０．１－７２小时；（３）净化处理；（４）过渡金属盐转化反应步骤，该步骤中，把净化处理所得产物在５０－１０００℃空气中煅烧０．５－７２小时，或者在５０－１０００℃氢气氛中煅烧０．５－７２小时，或者用可见光、紫外光照射０．１－７２小时。
【技术特征摘要】
【专利技术属性】
技术研发人员：马新起，郭新勇，金振声，杨建军，张治军，
申请(专利权)人：河南大学，
类型：发明
国别省市：41[中国|河南]