一种氟化铝催化剂的机械混合焙烧制备方法及其应用技术
Mechanical mixing roasting method for preparing aluminium fluoride catalyst and application thereof
The invention discloses a method for preparing a mechanical mixing roasting aluminum fluoride catalyst and 1,1,1,2 tetrafluoroethane cracking preparation and application of fluoride in three. The preparation method is that aluminum salt and fluorine polymer mixture, stirring evenly, and then placed in the muffle furnace for calcination of the aluminum fluoride catalyst. The method of synthesis of aluminum fluoride catalyst preparation has high catalytic activity in the reaction of three fluoride and good stability in 1,1,1,2 tetrafluoroethane pyrolysis, catalyst preparation process is simple, less steps, low equipment requirements, high efficiency, good repeatability.
【技术实现步骤摘要】
一种氟化铝催化剂的机械混合焙烧制备方法及其应用本专利技术属于一种金属氟化物催化剂制备
，具体涉及一种氟化铝催化剂的机械混合焙烧制备方法，该方法得到的氟化铝催化剂在1,1,1,2-四氟乙烷裂解制备三氟乙烯中的应用。
技术介绍
氟氯烃（CFCS）是工业上非常重要的一类化合物，其在作制冷剂、清洗剂、发泡剂、气雾剂、气雾推进剂等诸多领域有着广泛的应用。其中自20世纪以来HFC-134a作为制冷剂应用的最为广泛，但是氟氯烃非常的稳定，并且对大气臭氧层产生严重的破坏作用，同时是一种温室气体，严重危害着人类身体健康和生存环境，因此，HFC-134a的使用逐渐被其他制冷剂取代。HFC-134a的限制使用造成其生产过剩，三氟乙稀是HFC-134a脱HF的产物，是合成性能优异的含氟树脂、精细化学品以及功能型的高分子氟聚合物的重要高分子基础结构单元。HFC-134a的脱HF反应在较强Lewis酸位上进行，其中具有此强度Lewis酸位的催化剂中应用最广泛的为氟化铝。氟化铝是金属氟化物中最具代表性的一类无机材料，不仅作为融盐被广泛用于电解制备铝的生产中，同时也是作为光学玻璃组件的理想材料，...
【技术保护点】
一种氟化铝催化剂的机械混合焙烧制备方法，其特征在于将铝盐和含氟聚合物置于圆瓷皿中搅拌均匀，再放置于马弗炉中进行煅烧处理，缓慢升温至煅烧温度250‑600℃，并在该温度下保持3‑12h，煅烧结束冷却得氟化铝催化剂。
【技术特征摘要】
1.一种氟化铝催化剂的机械混合焙烧制备方法，其特征在于将铝盐和含氟聚合物置于圆瓷皿中搅拌均匀，再放置于马弗炉中进行煅烧处理，缓慢升温至煅烧温度250-600℃，并在该温度下保持3-12h，煅烧结束冷却得氟化铝催化剂。2.根据权利要求1所述的一种氟化铝催化剂的机械混合焙烧制备方法，其特征在于铝盐与含氟聚合物的投料质量比为1:0.5-5，优选为1:1-4。3.根据权利要求1所述的一种氟化铝催化剂的机械混合焙烧制备方法，其特征在于铝盐为硝酸铝、六水氯化铝、异丙醇铝、硫酸铝、氢氧化铝、草酸铝或醋酸铝中的一种或几种混合物，优选为硝酸铝、氢氧化铝、草酸铝或醋酸铝中的任意一种、两种或三种混合物。4.根据权利要求1所述的一种氟化铝催化剂的机械混合焙烧制备方法，...
【专利技术属性】
技术研发人员：韩文锋，习苗，王海丽，周胜兰，唐浩东，王志昆，
申请(专利权)人：浙江工业大学，
类型：发明
国别省市：浙江,33