一种注树脂胶模具制造技术
Resin injection mould
The utility model relates to a resin injection mold; including punch and die mould, assembly, U cavity mold mold and mold die forming an inverted U type cavity, the front inversion for imported glass fiber, U end cavity inverted for the product export. On the top of the front mould die is connected with the U type cavity inverted resin slot, the resin tank is connected through a resin inlet joint and resin inlet pipe; mould and die die in the back part is provided with a heating plate; has the advantages of simple structure, reasonable design, in the premise of ensuring the glass fiber and resin is not broken down the advantages, the tensile strength of FRP products, enhance shear strength, reduce production costs and improve production efficiency.
【技术实现步骤摘要】
一种注树脂胶模具
本技术属于制作注树脂胶玻璃钢制品
，具体涉及一种注树脂胶模具。
技术介绍
热固性树脂广泛用于制作玻璃钢、纽扣、胶粘剂和人造石等方面，尤其是在制作注树脂胶玻璃钢制品时，需要将玻璃纤维浸在树脂胶内，然后通过进入模具中加热固化成为成品；上述生产工艺存在着下列缺陷：1、由于成品中玻璃纤维含量低，树脂的含量过高，一方面造成了原材料树脂的浪费(树脂单价是玻璃纤维单价的两倍)，另一方面造成制作玻璃钢制品的成本增高；2、抗拉强度低，一般玻璃钢制品的抗拉强度为≤400Mpa；3、抗剪强度低，一般玻璃钢制品的抗剪强度≤110Mpa；4、生产效率低，一般玻璃钢制品每分钟能够生产≤0.5米；且工人的劳动强度大；5、耗电量高，一般1米玻璃钢制品的耗电量为0.3度；6、玻璃钢制品在生产过程中易造成较多的碎玻璃纤维和树脂洒落造成的浪费。
技术实现思路
本技术目的在于克服现有技术中的缺陷而提供一种结构简单、设计合理、生产成本低、在保证玻璃纤维不碎和树脂不洒落的前提下，使玻璃钢制品的抗拉强度增强到≥500MPa、抗剪强度增强到≥150MPa、玻璃钢制品每分钟能够生产≤2.5米和...
【技术保护点】
一种注树脂胶模具，其特征在于：该模具包括模具上模(2)和模具下模(7)，装配后，模具上模(2)和模具下模(7)之间形成一个倒置的U型腔体，倒置的U型腔体的前端为玻璃纤维进口(1)，倒置的U型腔体的末端为产品出口(10)，模具上模(2)前部的顶端设有与倒置的U型腔体相连通的树脂槽(6)，树脂槽(6)通过树脂进口接头(4)与树脂进口管道(5)相连；模具上模(2)和模具下模(7)的中后部设有加热板(8)。
【技术特征摘要】
1.一种注树脂胶模具，其特征在于：该模具包括模具上模(2)和模具下模(7)，装配后，模具上模(2)和模具下模(7)之间形成一个倒置的U型腔体，倒置的U型腔体的前端为玻璃纤维进口(1)，倒置的U型腔体的末端为产品出口(10)，模具上模(2)前部的顶端设有与倒置的U型腔体相连通的树脂槽(6)，树脂槽(6)通过树脂进口接头(4)与树脂进口管道(5)相连；模具上模(2)和模具下模(7)的中后部设有加热板(8)。2.根据权利要求1所述的一种注树脂胶模具...
【专利技术属性】
技术研发人员：康雯利，
申请(专利权)人：新乡市景龙复合材料有限公司，
类型：新型
国别省市：河南,41