The invention discloses a method for preparing polypropylene composition and preparation method thereof, wherein the polypropylene composition comprises polypropylene, glass fiber, rubber, talc, colorant, antioxidant, light stabilizer, the polypropylene 60-70 weight portions, rubber 5-15 weight, glass fiber 22-32 weight, the weight of 0.5-1.5 colorant a, antioxidant 0.2-0.4 weight, light stabilizer 0.2-0.9 weight. Polypropylene material composition and preparation method thereof provided by the invention, because the existing polypropylene block copolymer (PP-B) added to the rubber and glass fiber, and in the preparation process of barrel twin-screw extruder from the feeding port to the die is divided into five sections of temperature control, the temperature of each section as follows 200 c, 210 C, 210 C, 220 C and 200 c, the products with high impact toughness, high modulus and other properties.
【技术实现步骤摘要】
本专利技术涉及，特别是涉及一种高冲击，高模 量的聚丙烯材料组合物及其制备方法。
技术介绍
聚丙烯材料具有可塑性和很好的耐热性，加工性能良好，具有优良的电绝缘性，有 很好的化学和热化学稳定性，广泛用于汽车零部件。但是由于汽车中塑料制品对材料性能 的要求较高，通常要经过改性的聚丙烯材料才能符合汽车中材料的高性能要求。而目前多 数的改性方法是用滑石粉填充，他的缺点是加了橡胶后刚性下降很多。而玻璃纤维是一种 性能优异的无机非金属材料。英文原名为glass fiber。玻璃纤维单丝的直径从12个微 米到二十几米个微米，相当于一根头发丝的1/20-1/5，每束纤维原丝都有数百根甚至上千 根单丝组成，通常作为复合材料中的增强材料，电绝缘材料和绝热保温材料等，广泛应用于 国民经济各个领域。它优良的性能指标主要体现在拉伸强度高，伸长小(3%)、弹性系数 高，刚性佳、弹性限度内伸长量大且拉伸强度高、加工性佳、价格便宜，更适合应用于仪表骨 架，手套箱等要求强度高的产品。
技术实现思路
针对上述问题，本专利技术的主要目的在于提供一种聚丙烯材料组合物及其制备方 法，该聚丙烯材料组合物具有高冲...
【技术保护点】
１．一种聚丙烯材料组合物，其特征在于所述聚丙烯材料组合物包括聚丙烯，橡胶，玻璃纤维，着色剂，抗氧剂，光稳定剂，所述的聚丙烯为６０－７０重量份，橡胶５－１５重量份，玻璃纤维２２－３２重量份，着色剂０．５－１．５重量份，抗氧剂０．２－０．４重量份，光稳定剂０．２－０．９重量份。
【技术特征摘要】
【专利技术属性】
技术研发人员：罗琨，
申请(专利权)人：上海继尔新材料科技有限公司，罗琨，
类型：发明
国别省市：31