本发明专利技术提供一种制备脱硝整体式催化剂的浆料，其包括催化剂、硅胶和水，还提供一种采用浸渍法制备脱硝整体式催化剂的方法。相对于现有技术，本发明专利技术的浆料中不含任何有机溶剂，不仅简单、环保，而且可以降低生产成本；本发明专利技术制备出的整体式催化剂具有较高的脱硝活性及较宽的温度窗口，而且催化剂的涂覆量可以通过调变浆液中催化剂的浓度来实现，仅需一次涂覆便可得到目标涂覆量，从而大大的缩短制备过程，大幅度的降低生产成本，也就更适合大规模的生产。

Method for preparing denitration monolithic catalyst and slurry thereof

The present invention provides a slurry for the preparation of a denitration monolithic catalyst comprising a catalyst, silica gel and water, and a process for the preparation of a denitration integral catalyst by impregnation. Compared with the prior art, does not contain any organic solvent slurry of the invention, not only simple, environmentally friendly, and can reduce the production cost; monolithic catalyst prepared by the invention has high denitrification activity and a wide temperature window, the concentration and amount of catalyst slurry can be coated by changing the catalyst to achieve only once, we can get the target coated coating amount, thus greatly shortening the preparation process, greatly reduce the production cost, is more suitable for large scale production.

【技术实现步骤摘要】

本专利技术涉及一种氮氧化物还原的催化材料领域，尤其是一种脱硝整体式催化剂的制备方法及其简单、环保的浆料。
技术介绍
近年来，柴油机以其优良的燃油经济性与动力性能而备受青睐，但柴油机存在的一个最大问题就是氮氧化物排放严重。氮氧化物包括有NO、NO2, N2O, N2O3> N2O4和队05等， 各种燃料燃烧过程中产生的NOx主要是N0，约占90% 95%，NO2占5% 10%，N2O仅占左右，NO和NO2统称为N0X。氮氧化物(NOx)对大气的污染是一个世界性的环境问题，它的影响主要表现为形成酸雨、导致光化学烟雾、造成近地层大气臭氧污染、产生温室效应、 破坏自然生态环境等。此外，NOx也参与形成空气中的飘尘(PM2.5)，严重危害人类健康。因此，限制柴油机NOx排放的法规也从无到有，从宽松到严格，如何降低车用柴油机NOx排放的研究显得尤为重要。目前，选择性催化还原(SCR，即selective catalytic reduction)脱硝技术以其高达90%的脱硝率成为当前世界上主流的脱硝技术。SCR脱硝，是在催化剂存在的情况下，采用氨类物质、CO、碳氢化合物为还原剂，也可以利用本文档来自技高网...

【技术保护点】
１．一种制备脱硝整体式催化剂的浆料，其特征在于：包括催化剂、硅胶和水。

【技术特征摘要】

【专利技术属性】
技术研发人员：萧剑鸣，赵向云，韩晖，汪加林，刘定学，计美香，范群，
申请(专利权)人：广州市威格林环保科技有限公司，
类型：发明
国别省市：81