一种氯氧化钐纳米片及其制备方法和应用技术

本发明专利技术公开了一种氯氧化钐纳米片及其制备方法和应用，其结构为非晶态烟雾状二维氯氧化钐纳米片，制备过程为：(1)先将三羟甲基氨基甲烷和盐酸混合得到缓冲液，再加入可溶性钐源和氧化石墨烯超声处理得到分散均匀的悬浊液，反应后经固液分离、干燥后得到前驱体；(2)前驱体于500‑600℃下灼烧即得氧化钐纳米片。本发明专利技术的非晶态烟雾状二维氯氧化钐纳米片用作光催化N

Samarium oxychloride Nanoflake and its preparation and Application

The invention discloses a samarium oxychloride nano sheet and its preparation method and application. Its structure is amorphous smoke like two-dimensional samarium oxychloride nano sheet. The preparation process is as follows: (1) first mix the trihydroxymethyl aminomethane and hydrochloric acid to get buffer solution, then add the soluble samarium source and oxyfossil graphene to get the uniformly dispersed suspension after ultrasonic treatment, and then separate and dry the solid-liquid to get The precursor; (2) the precursor is burned at 500 \u2011 600 \u2103 to obtain the sm2o nano sheet. The amorphous smoky two-dimensional samarium oxychloride nano sheet of the invention is used as photocatalysis n

【技术实现步骤摘要】
一种氯氧化钐纳米片及其制备方法和应用
本专利技术属于光催化合成氨
，具体涉及一种非晶态烟雾状二维氯氧化钐纳米片及其制备方法，并作为光催化合成氨催化剂的应用。
技术介绍
稀土氧化物以其独特的性质成为重要的新兴材料。但目前学界对稀土氧化物的制备方法主要局限于稀土氧化物超微粒子的合成研究，对于二维稀土氧化物的合成方法研究较少，目前的合成方法比较少只有类似于矿化剂法等很少的一些方法。从制备方法而言,稀土基的卤氧化物使用传统的固相反应，一般需要较高的温度,比如900摄氏度。但是,传统的固相反应无法获得纳米尺度的稀土卤氧化物。对于稀土卤氧化物的合成方法的研究，至今主要限制在块体材料和薄膜方面。关于稀土卤氧化物的纳米材料研究，只有零星的报道。比如严纯华等人使用(La(CCl3COO)3)单源前驱体在十八烯和长链胺溶液中通过热分解,制备了卤氧化镧。SarbajitBanerjee等人报道了使用LnCl3和Ln(O'Pr)3合成了LnOCl(Ln＝La,Ce,Gd,Dy,Er,Yb)纳米晶(KennethR.KortandSarbajitBanerjee,本文档来自技高网...

【技术保护点】
1.一种氯氧化钐纳米片，其特征在于：其结构为非晶态烟雾状二维氯氧化钐纳米片。/n

【技术特征摘要】
1.一种氯氧化钐纳米片，其特征在于：其结构为非晶态烟雾状二维氯氧化钐纳米片。


2.权利要求1所述的一种氯氧化钐纳米片的制备方法，其特征在于，包括如下步骤：
(1)先将三羟甲基氨基甲烷和盐酸混合得到缓冲液，再加入可溶性钐源和氧化石墨烯超声处理得到分散均匀的悬浊液，反应后经固液分离、干燥后得到前驱体；
(2)前驱体于500-600℃下灼烧即得氧化钐纳米片。


3.根据权利要求2所述的一种氯氧化钐纳米片的制备方法，其特征在于：步骤(1)中，步骤(1)中，所述三羟甲基氨基甲烷和盐酸混合得到的缓冲液的pH为7.0～8.0。


4.根据权利要求2所述的一种氯氧化钐纳米片的制备方法，其特征在于：步骤(1)中，所述可溶性钐源选自氯化钐和硝酸钐中的一种或几种，可溶性钐源的加入量为1～5mg/ml。


5.根据权利要求2所述的一种氯氧化钐纳米片的制备...

【专利技术属性】
技术研发人员：王梁炳，郭瑞晗，侯婷婷，杨国，
申请(专利权)人：中南大学，
类型：发明
国别省市：湖南;43