The invention relates to a lithium ion battery negative electrode, which comprises a flexible self-supporting carbon nanotube film and a plurality of titanium dioxide nanoparticles. The self-supporting carbon nanotube film comprises a plurality of carbon nanotubes. The plurality of titanium dioxide nanoparticles are uniformly adsorbed on the surface of a plurality of carbon nanotubes, and the titanium dioxide nanoparticles are uniformly adsorbed on the surface of the plurality of carbon nanotubes. The particle size is less than or equal to 30 nm. The invention also provides a flexible lithium ion battery using the anode of the lithium ion battery.
【技术实现步骤摘要】
锂离子电池负极及柔性锂离子电池
本专利技术涉及一种锂离子电池负极及柔性锂离子电池，尤其涉及一种基于碳纳米管的锂离子电池负极及柔性锂离子电池。
技术介绍
碳纳米管(carbonnanotube,CNT)是近年来发现的一种新型碳系材料，由单层或多层的石墨片状结构卷曲而成。碳纳米管的层间距为0.34纳米，略大于石墨的层间距，有利于锂离子的嵌入和脱出。碳纳米管作锂离子电池负极材料，锂离子不仅可嵌入中空管内，而且可嵌入到层间的缝隙、空穴之中，具有嵌入深度小、过程短，嵌入位置多等优点。另外，碳纳米管具有优良的导电性，如果将碳纳米管加入到锂离子电池的负极材料中，可以提高锂离子电池负极材料的导电性。然而，传统的碳纳米管负极能量密度较小，且在锂插入/脱嵌过程中具有较大的晶格变化以及较低的工作电压，不能避免电极塌陷，以及抑制负极上固体电解质界面(SEI)层和锂枝晶的形成。
技术实现思路
有鉴于此，确有必要提供一种可以避免电极塌陷，以及抑制负极上固体电解质界面(SEI)层和锂枝晶的形成的锂离子电池负极。一种锂离子电池负极，包括一具有柔性的自支撑碳纳米管膜以及多个二氧化钛纳米颗粒，该自支撑碳...
【技术保护点】
1.一种锂离子电池负极，其特征在于，包括一具有柔性的自支撑碳纳米管膜以及多个二氧化钛纳米颗粒，该自支撑碳纳米管膜包括多个碳纳米管，该多个二氧化钛纳米颗粒均匀吸附在多个碳纳米管的表面，且该二氧化钛纳米颗粒的粒径小于等于30纳米。
【技术特征摘要】
1.一种锂离子电池负极，其特征在于，包括一具有柔性的自支撑碳纳米管膜以及多个二氧化钛纳米颗粒，该自支撑碳纳米管膜包括多个碳纳米管，该多个二氧化钛纳米颗粒均匀吸附在多个碳纳米管的表面，且该二氧化钛纳米颗粒的粒径小于等于30纳米。2.如权利要求1所述的锂离子电池负极，其特征在于，所述二氧化钛纳米颗粒的粒径大于等于3纳米小于等于10纳米。3.如权利要求1所述的锂离子电池负极，其特征在于，所述多个二氧化钛纳米颗粒在所述多个碳纳米管的表面形成一连续的二氧化钛层。4.如权利要求3所述的锂离子电池负极，其特征在于，该连续的二氧化钛层的厚度大于等于3纳米小于等于20纳米。5.如权利要求1所述的锂离子电池负极，其特征在于，所述多个二氧化钛纳米颗粒间隔且均匀的分散在所述多个碳纳米管的表面。6.如权利要求1所述的锂离子电池负极，其特征在于，所述二氧化钛纳米颗粒在所述锂离子电池负极中的质量百分比大于等于20％小于等...
【专利技术属性】
技术研发人员：朱坤磊，刘锴，王佳平，姜开利，范守善，
申请(专利权)人：清华大学，鸿富锦精密工业深圳有限公司，
类型：发明
国别省市：北京,11