The invention relates to a processing technology of electric wires, which belongs to the technical field of power distribution equipment. The processing technology of the wire includes the following steps: a single wire drawing; two monofilament annealing, made of metal monofilament; three removal of metal monofilament from oil; four to clean and passivate metal monofilament; five to tinplate metal monofilament; six twisted wire; seven will make the first preheating of the wire, and heat to 200 c to 80 C after 200 centigrade; eight wire The second preheating is heated to 180 degrees; nine, the wire is fed into the extruder to wrap the rubber, and the insulating layer is coated to make the wires. The wire processing technology of the invention can produce metal monofilaments by annealing, thereby improving the quality of the metal monofilament and prolonging the service life.
【技术实现步骤摘要】
一种电线的加工工艺
本专利技术涉及一种电线的加工工艺，属于配电设备
技术介绍
电线是指传输电能的导线。分裸线、电磁线和绝缘线。裸线没有绝缘层，包括铜、铝平线、架空绞线以及各种型材(如型线、母线、铜排、铝排等)。它主要用于户外架空及室内汇流排和开关箱。电磁线是通电后产生磁场或在磁场中感应产生电流的绝缘导线。它主要用于电动机和变压器绕圈以及其他有关电磁设备。其导体主要是铜线，应有薄的绝缘层和良好的电气机械性能，以及耐热、防潮、耐溶剂等性能。选用不同的绝缘材料可获得不同的特性。现有技术中，导电线的线芯通常使用金属单丝拉拔制作，由金属细丝经拉拔退火拉拔至微丝后集合成束，经绞捻而成；金属单丝拉拔通常只能拉拔至0.03mm丝径，而继续拉拔变细工艺复杂，生产效率和成品率都很低，且成本上升。现有多芯电线由于经多根合股绞捻而成，由于丝径较粗，其耐弯折能力较差，在小曲率如曲率半径为1mm弯曲时，多芯电线会形成塑性变形不能回弹，因此不耐折易断；现有多芯电线如果单丝折断可能刺破绝缘层而漏电。国内外市场以氟塑料为绝缘的各种高温电线电缆最为普遍，尤其是以XETFE为绝缘、护套材料的...
【技术保护点】
一种电线的加工工艺,其特征在于：包括以下步骤：㈠单丝拉制，在55‑65℃的条件下，利用拉丝机，经过拉伸模具，将紫铜棒材拉伸，拉丝的直径为在25um‑30um；㈡单丝退火，通过退火炉进行退火，退火温度400‑450℃，退火时间15‑20分钟，制成金属单丝；㈢将金属单丝脱脂除油；㈣将金属单丝清洗钝化；㈤将金属单丝镀锡，即将清洗钝化后的金属单丝立即放入温度在25℃～35℃镀锡液中，传输速度控制在6~8m/s，电流密度控制在20～35a/dm
【技术特征摘要】
1.一种电线的加工工艺,其特征在于：包括以下步骤：㈠单丝拉制，在55-65℃的条件下，利用拉丝机，经过拉伸模具，将紫铜棒材拉伸，拉丝的直径为在25um-30um；㈡单丝退火，通过退火炉进行退火，退火温度400-450℃，退火时间15-20分钟，制成金属单丝；㈢将金属单丝脱脂除油；㈣将金属单丝清洗钝化；㈤将金属单丝镀锡，即将清洗钝化后的金属单丝立即放入温度在25℃～35℃镀锡液中，传输速度控制在6~8m/s，电流密度控制在20～35a/dm2；㈥绞制，由至少两股金属单丝合股捻制而成导线，采用压紧机对导线进行紧压；㈦将制得的导线进行第一次预热...
【专利技术属性】
技术研发人员：刘浩，张君，张欢芬，
申请(专利权)人：苏州浩焱精密模具有限公司，
类型：发明
国别省市：江苏,32