A preparation method of polyprolactone and L-polylactic acid blends, which belongs to the field of material preparation. The utility model is characterized in that a PLLA electric heating drying box for drying; PCL, PLLA and TBC were blended in the twin-screw extruder, the screw speed of 200R / min; each 100g PCL / PLLA blends with 8gTBC; the resulting blend granulating and drying after vulcanizing apparatus at 170 DEG C melting pressure made of thin. By improving the traditional process, the mixture was prepared, and the compatibility of the mixture was improved by adding three butyl citrate into the mixture, so that the material had better shape memory function. The preparation process of the polyprolactone and L-polylactic acid blends is simple and easy to operate, and is suitable for the popularization and use of the blends.
【技术实现步骤摘要】
一种聚已内酯与左旋聚乳酸共混物的制备方法
本专利技术属于材料制备领域，尤其涉及一种聚已内酯与左旋聚乳酸共混物的制备方法。
技术介绍
随着材料科技的快速发展，以及医疗技术的进步，在现代医学中有越来越多的新材料被作为修复材料等应用，聚己内酯(PCL)是由ε-己内酯经过开环聚合而成的一种新型聚合物，由于其优良的生物降解性、生物相容性和可加工性，因而在生物医学工程等领域有着许多潜在的应用价值。但是由于PCL的熔点较低，只有60℃左右，耐热变形性能较差，在医学上作为修复材料、矫形固定材料和组织工程支架材料使用时，其硬度和强度都不能满足要求，因此有必要对PCL进行改性。
技术实现思路
本专利技术旨在解决上述问题，提供一种聚已内酯与左旋聚乳酸共混物的制备方法。一种聚已内酯与左旋聚乳酸共混物的制备方法，其特征在于：将PLLA置于电热干燥箱中干燥；将PCL、PLLA和TBC在双螺杆挤出机中进行共混，螺杆转速200r／min；其中每100gPCL／PLLA共混物添加8gTBC；所得共混物经造粒、干燥后经平板硫化仪于170℃熔融压制成薄片。本专利技术所述的一种聚已内酯与左旋聚乳酸共混物的制...
【技术保护点】
一种聚已内酯与左旋聚乳酸共混物的制备方法，其特征在于：将PLLA置于电热干燥箱中干燥；将PCL、PLLA和TBC在双螺杆挤出机中进行共混，螺杆转速200r／min；其中每100g PCL／PLLA共混物添加8g TBC；所得共混物经造粒、干燥后经平板硫化仪于170℃熔融压制成薄片。
【技术特征摘要】
1.一种聚已内酯与左旋聚乳酸共混物的制备方法，其特征在于：将PLLA置于电热干燥箱中干燥；将PCL、PLLA和TBC在双螺杆挤出机中进行共混，螺杆转速200r／min；其中每100gPCL／PLLA共混物添加8gTBC；所得共混物经造粒、干燥后经平板硫化仪于170℃熔融压制成薄片。2.如权利要求1所述的一种聚已内酯与左旋聚乳酸共混物的制备方法，其特征在于所述PLLA的质量分数为20%。3.如权利要求1所述的一种聚已内酯与左旋聚乳酸共混物的制备方法，其特征在于所述挤出机从料筒到...
【专利技术属性】
技术研发人员：王耀斌，
申请(专利权)人：陕西盛迈石油有限公司，
类型：发明
国别省市：陕西,61