本发明专利技术公开了一种炉头用高硼含量的硼不锈钢的制备方法，包括以下步骤：1）制备含硼的不锈钢原材料；2）将含硼的不锈钢原材料装在挤压筒中进行封装，保温直至粉料完全热透，再挤压形成板坯；3）将板坯轧制成成品，本发明专利技术具有工艺流程短，硼化物在制备过程中损失少，没有漫长的烧结过程，含硼化合物在不锈钢基体中分布均匀，材料的机械性能优良等优点。

A preparation method of boron stainless steel with high boron content for furnace head

The invention discloses a preparation method of high boron content of boron stainless steel furnace head, which comprises the following steps: 1) the raw material preparation of boron stainless steel; 2) raw materials containing boron in stainless steel tube extrusion packaging, insulation powder until heated through, then extrusion forming slab 3); the blank is rolled into a finished product, the invention has the advantages of short process, less loss of borides in the preparation process, no sintering process long, uniform distribution of boron compounds on the stainless steel, good mechanical properties of materials.

【技术实现步骤摘要】
一种炉头用高硼含量的硼不锈钢的制备方法
本专利技术属于铸造
，具体涉及一种炉头用高硼含量的硼不锈钢的制备方法。
技术介绍
硼不锈钢是硼化物的均匀弥散在不锈钢基体中形成的一种合金。硼的加入会导致材料的机械性能、腐蚀性能、加工性能等的大幅劣化。所以如何保证在加入适当的硼后，材料的综合性能良好，这对材料的制备工艺提出了较高的要求，这也是我国一直没有硼不锈钢制造技术的原因，所以加强对硼不锈钢的研究有重要意义。
技术实现思路
为了克服现有
存在的上述技术问题，本专利技术的目的在于，提供一种炉头用高硼含量的硼不锈钢的制备方法，解决由于硼的加入导致含硼不锈钢材料塑性差、成型困难的问题。本专利技术提供的一种炉头用高硼含量的硼不锈钢的制备方法，包括以下步骤：1）制备含硼的不锈钢原材料；2）将含硼的不锈钢原材料装在挤压筒中进行封装，在900℃-1200℃之间保温直至粉料完全热透，再挤压形成板坯，挤压应变速率为0.01-5s-1，挤压比在6-10之间；3）将板坯轧制成成品。本专利技术提供的一种炉头用高硼含量的硼不锈钢的制备方法，其有益效果在于，通过挤压筒挤压形成板坯，再将板坯轧制成成品的方法，有效克服了含硼不锈钢材料塑性差、成型困难的问题，使本专利技术方法的操作过程更加简单、易控制，并使成型成品的尺寸可控，同时能有效提高成品综合性能。具体实施方式下面结合一个实施例，对本专利技术提供的一种炉头用高硼含量的硼不锈钢的制备方法进行详细的说明。实施例本实施例的一种炉头用高硼含量的硼不锈钢的制备方法，包括以下步骤：1）制备含硼的不锈钢原材料；2）将含硼的不锈钢原材料装在挤压筒中进行封装，在1200℃之间保温直至粉料完全热透，再挤压形成板坯，挤压应变速率为5s-1，挤压比10；3）将板坯轧制成成品。本文档来自技高网...

【技术保护点】
一种炉头用高硼含量的硼不锈钢的制备方法，其特征在于：包括以下步骤：1）制备含硼的不锈钢原材料；2）将含硼的不锈钢原材料装在挤压筒中进行封装，在900℃‑1200℃之间保温直至粉料完全热透，再挤压形成板坯，挤压应变速率为0.01‑5

【技术特征摘要】
1.一种炉头用高硼含量的硼不锈钢的制备方法，其特征在于：包括以下步骤：1）制备含硼的不锈钢原材料；2）将含硼的不锈钢原材料装在挤压筒中进行封装...

【专利技术属性】
技术研发人员：李玉敏，
申请(专利权)人：青岛天地铸造有限公司，
类型：发明
国别省市：山东,37