The invention belongs to the field of air pollution control technology and environmental protection catalytic material technology, in particular to a kind of complex oxide catalyst technology field for decomposing N2O. A kind of catalysts for the decomposition of N2O, which is characterized in that the catalyst with gamma Al2O3 composite oxide as active component, Co, Ni, Ba, Mn, Fe and Mg as additives, content of active components of gamma Al2O3 load is 0.5% ~ 35%, the quality of content to help the catalyst load is 0.5% ~ 22%; the molar ratio of Co, Co/Ni/Ba/Mn/Fe/Mg elements Ni, Ba, Mn, Fe, Mg in (0.2 ~ 3): (0.1 ~ 1): (0.5 ~ 2): (1 ~ 3): (0.5 ~ 1.5): (0.1 ~ 0.5), can be used in treating industrial waste gas containing N2O, reduce environmental pollution, wide application prospect.
【技术实现步骤摘要】
一种用于分解N2O的复合氧化物催化剂及其制备方法
本专利技术属于大气污染治理技术和环保催化材料
，特别涉及一种用于分解N2O的复合氧化物催化剂
技术介绍
N2O是大气中主要温室气体之一，它不仅能产生温室效应，而且还严重污染着大气环境。N2O为痕量气体，其对温室效应的贡献是CH4的2.5倍。同时，其全球增暖潜能是CO2的310倍。N2O气体的人为污染源主要有己二酸和硝酸生产，矿物燃料燃烧，生物质分解，农田耕作和汽车尾气等。随着工业化进程的提高和机动车数量的急剧增加，大气中的N2O含量正在逐渐上升，超过了大气自平衡能力，严重破坏着大气环境。因此，减少N2O排放技术成为了重点研究对象。用于催化分解N2O的催化剂经历了从贵金属、氧化物到混合氧化物、负载型催化剂等一系列的演变。负载型催化剂的载体也由简单的SiO2、γ-Al2O3等向种类丰富的沸石、分子筛等载体拓展。负载型催化剂具有高比表面积、高分散的特性，能充分发挥活性组分的催化活性，具有很好的应用前景。其中，专利(CN102513117A)是以Cu-Ce金属复合氧化物作为催化剂，该催化剂低温活性高。不足的...
【技术保护点】
一种用于分解N2O的复合氧化物催化剂，其特征在于，催化剂以γ‑Al2O3复合氧化物为活性组分，以Co、Ni、Ba、Mn、Fe、Mg为助剂，活性组分γ‑Al2O3负载的质量百分含量为0.5％～35％，助催化剂负载的质量百分含量为0.5％～22％；所述Co、Ni、Ba、Mn、Fe、Mg中Co/Ni/Ba/Mn/Fe/Mg元素摩尔比为(0.2～3)：(0.1～1)：(0.5～2)：(1～3)：(0.5～1.5)：(0.1～0.5)。
【技术特征摘要】
1.一种用于分解N2O的复合氧化物催化剂，其特征在于，催化剂以γ-Al2O3复合氧化物为活性组分，以Co、Ni、Ba、Mn、Fe、Mg为助剂，活性组分γ-Al2O3负载的质量百分含量为0.5％～35％，助催化剂负载的质量百分含量为0.5％～22％；所述Co、Ni、Ba、Mn、Fe、Mg中Co/Ni/Ba/Mn/Fe/Mg元素摩尔比为(0.2～3)：(0.1～1)：(0.5～2)：(1～3)：(0.5～1.5)：(0.1～0.5)。2.一种制备如权利要求1所述的用于分解N2O的Cu-Zn复合氧化物催化剂的方法，具体步骤为：S1，按质量比Cu：Z...
【专利技术属性】
技术研发人员：李群，曾光，
申请(专利权)人：武汉兴天宇环境股份有限公司，
类型：发明
国别省市：湖北,42