一种水处理材料及其应用制造技术

本发明专利技术涉及一种臭氧去除水中有机污染的添加剂，所述添加剂是固体催化剂，该固体催化剂是锰铁复合催化剂，采用水热法合成。本发明专利技术采用无毒无害原料，制备出具有催化活性高、抗湿性能好、催化分解臭氧量高、去除有机污染物效率高等特点的锰铁复合催化剂，制备方法简单，可重复性高，适于工业化生产，所得复合催化剂适用于去除家庭、工业生产过程中产生的臭氧，亦适用于催化臭氧去除水源水中有机污染物。

A kind of water treatment material and its application

The invention relates to an additive for ozone to remove organic pollutants in water. The additive is a solid catalyst, and the solid catalyst is a ferromanganese composite catalyst and is synthesized by hydrothermal method. The invention adopts non-toxic and harmless raw materials, prepared with high catalytic activity, good moisture resistance and catalytic decomposition of ozone content and high removal efficiency of organic pollutants of higher manganese composite catalyst, preparation method is simple, reproducible and suitable for industrial production, the composite catalyst is suitable for ozone removal, family produced in, and is also suitable for catalytic ozonation of organic pollutants in source water.

【技术实现步骤摘要】
一种水处理材料及其应用
本专利技术涉及一种锰铁复合催化剂材料，涉及该材料的制备方法以及该材料在水处理领域以及空气处理中的应用。
技术介绍
随着社会经济和工业生产的不断发展，环境污染越来越严重，环境的恶化严重影响了人类的生活质量和生产活动，已经成为全球性普遍关注的重要课题。近年来我国的水源普遍遭到污染，且呈发展趋势，水源污染使原有的水处理工艺受到前所未有的挑战。目前生物处理技术由于其经济实用等优点已在水处理领域得到了广泛应用。然而当水体中存在毒性难生物降解有机污染物时（例如2,4-二氯苯氧乙酸），会使生物技术难以实施。因此需要探索和研究更为经济有效的水处理的新技术和新方法。臭氧氧化技术是一种环境友好的水处理技术，近些年来得到广泛研究并应用于水体中有机污染物的去除。但是由于臭氧本身的一些理化性质，使之在水体中反应时具有较强的选择性，很难将原水中的有机物矿化完全。随之发展而来的多相催化臭氧氧化技术是一种新型的高级氧化工艺，它能提高臭氧的利用效率同时提高水中有机污染物的去除效率。催化臭氧化技术在众多研究中显现出的巨大优势，有望成为一种应用于实际水体的水处理技术。臭氧是一种不稳定气体，具有刺激本文档来自技高网...

【技术保护点】
一种锰铁复合催化剂，其特征在于，其以蜂窝陶瓷为基础，包含占蜂窝陶瓷质量20‑25%的氧化铝涂层，氧化铝涂层外另外负载了占氧化铝涂层质量1‑10%的活性催化剂组分，所述活性催化剂组分为锰铁复合催化剂。

【技术特征摘要】
1.一种锰铁复合催化剂，其特征在于，其以蜂窝陶瓷为基础，包含占蜂窝陶瓷质量20-25%的氧化铝涂层，氧化铝涂层外另外负载了占氧化铝涂层质量1-10%的活性催化剂组分，所述活性催化剂组分为锰铁复合催化剂。2.根据权利要求1所述的复合催化剂，其特征在于，锰铁复合催化剂由水热法制备得到。3.一种使用权利要求1所述的锰铁复合催化剂去除水中有机污染物的方法，其特征在于，包括如下步骤：(1)取水厂水源水，经过滤泥沙和悬浊物后备用...

【专利技术属性】
技术研发人员：段仲达，
申请(专利权)人：绍兴上虞易诚工业设计有限公司，
类型：发明
国别省市：浙江,33