一种接枝共聚物及其制备方法技术

本发明专利技术公开了一种接枝共聚物及其制备方法，包括分别配置过硫酸钾溶液、甲基丙烯磺酸钠溶液和甲氧基聚氧乙烯醚溶液，然后将其在合适的温度下进行反应，然后使用异丙醇和甲醇进行清洗后得到接枝共聚物。本发明专利技术的接枝共聚物为两亲性高分子，具有高分子量，高磺化度，高亲水性；其主体结构单元为疏水基团、磺酸基和醚长链亲水，该接枝共聚物作为水煤浆分散剂应用效果显著，降黏效果好，分散效果良好。

Graft copolymer and preparation method thereof

The invention discloses a graft copolymer and a preparation method thereof, including configuration of potassium persulfate solution, sodium Methallyl sulfonate solution and methoxy polyoxyethylene ether solution, and then the reaction was carried out under suitable temperature, then using isopropanol and methanol were obtained after cleaning graft copolymer. The graft copolymer of the present invention is two amphiphilic polymer with high molecular weight, high sulfonation degree, high hydrophilicity; its main structure unit as the hydrophobic group, ether sulfonic acid and long chain hydrophilic, the graft copolymer as dispersant of coal water slurry application effect, viscosity reducing effect, good dispersion effect.

【技术实现步骤摘要】
一种接枝共聚物及其制备方法
本专利技术属于木质素磺酸盐
，涉及一种LS、SMAS或APEG接枝共聚物；还涉及上述接枝共聚物的制备方法。
技术介绍
木质素磺酸盐来源广泛，应用较广。聚醚类分散剂是一种新型的高效非离子型分散剂，它具有在较低掺量下减水率高、分散性能好、对环境无污染等特点，木质素磺酸钠、甲基丙烯磺酸钠、甲氧基聚氧乙烯醚的接枝共聚物属于两亲性高分子，水溶性良好、相对分子质量较高和降粘效果比较好。因此结合聚醚型分散剂对木质素磺酸盐进行改性处理有利于提高木质素磺酸盐实际应用效果。
技术实现思路
本专利技术提供了一种接枝共聚物，该共聚物以过硫酸钾为引发剂，采用甲基丙烯磺酸钠、甲氧基聚氧乙烯醚为接枝单体，具有高分散性、水溶性好、降粘效果好。用于水煤浆添加剂，分散效果显著。本专利技术还提供了上述接枝共聚物的制备方法，本专利技术的技术方案是：一种接枝共聚物，该共聚物的化学结构式为：本专利技术的另一技术方案是：上述接枝共聚物的制备方法，包括以过硫酸钾为引发剂，采用甲基丙烯磺酸钠和甲氧基聚氧乙烯醚为接枝单体进行化学反应，然后使用异丙醇、无水乙醇依次洗涤粗产物，抽滤、干燥后得到接枝共聚物。具体本文档来自技高网...

【技术保护点】
一种接枝共聚物，其特征在于，该共聚物的化学结构式为：

【技术特征摘要】
1.一种接枝共聚物，其特征在于，该共聚物的化学结构式为：2.一种如权利要求1所述的接枝共聚物的制备方法，其特征在于，包括以过硫酸钾为引发剂，采用甲基丙烯磺酸钠和甲氧基聚氧乙烯醚为接枝单体进行化学反应，然后使用异丙醇、无水乙醇依次洗涤粗产物，抽滤、干燥后得到接枝共聚物。3.根据权利要求2所述的接枝共聚物的制备方法，其特征在于，所述制备接枝共聚物的具体包括以下步骤：步骤1，按质量份数取5-40份的甲基丙烯磺酸钠，将其溶于质量份数为100份的蒸馏水中，搅拌均匀，后得到溶液A；步骤2，按质量份数取0.2-0.5份的过硫酸钾，在氮气环境中向过硫酸钾滴加质量份数为20份的水，之后得到溶液B；步骤3，按质量份数取5-...