The present invention relates to a light curing resin and its preparation and curing method, UV curing resin, by weight, which comprises: 70 resin 130, including acrylic resin, epoxy resin and silicone resin; coupling agent: 0.5 1; catalyst: 0.5 solvent: 1; 30 80. In the present invention, a low surface energy hybrid curable resin with double bond and epoxy group is obtained by a series of chemical graft reactions under the condition of catalyst and heating with a series of resins. The resin could improve the disadvantages of traditional silicon resin adhesion to the substrate, on the other hand can reduce the traditional Acrylic UV curing resin with high shrinkage defects in the high-end areas such as automotive, shipbuilding and other industries has been widely used.
【技术实现步骤摘要】
光固化树脂及其制备和固化方法
本专利技术涉及树脂合成领域，特别是涉及一种光固化树脂及其制备和固化方法。
技术介绍
光固化树脂由于其固化速度快、环境友好、能源消耗量少、无溶剂挥发等众多突出优点而得到广泛研究，并且在各行各业中迅速推广。但目前光固化树脂的表面能普遍较高，限制了其应用。而低表面能光固化树脂表面张力低、水接触角大，可用于防水防污以及自清洁领域。但低表面能的光固化树脂对基材的附着普遍较差，限制了其在船舶、汽车行业等高端领域的应用。
技术实现思路
本专利技术的目的是为了解决现有技术中存在的缺点，而提出的一种新型的光固化树脂及其制备和固化方法。为了实现上述目的，本专利技术采用了如下技术方案：本专利技术提出的一种光固化树脂，以重量份计，其包括：树脂：70-130份，包括丙烯酸树脂、环氧树脂和有机硅树脂；偶联剂：0.5-1份；催化剂：0.5-1份；溶剂：30-80份。优选的，前述的光固化树脂，以重量份计，其包括：丙烯酸树脂：50-80份；环氧树脂：10-30份；有机硅树脂：10-20份；偶联剂：0.5-1份；催化剂：0.5-1份；丙酮：20-45份；甲苯：10-35份。...
【技术保护点】
一种光固化树脂，其特征在于，以重量份计，其包括：树脂：70‑130份，包括丙烯酸树脂、环氧树脂和有机硅树脂；偶联剂：0.5‑1份；催化剂：0.5‑1份；溶剂：30‑80份。
【技术特征摘要】
1.一种光固化树脂，其特征在于，以重量份计，其包括：树脂：70-130份，包括丙烯酸树脂、环氧树脂和有机硅树脂；偶联剂：0.5-1份；催化剂：0.5-1份；溶剂：30-80份。2.根据权利要求1所述的光固化树脂，其特征在于，以重量份计，其包括：丙烯酸树脂：50-80份；环氧树脂：10-30份；有机硅树脂：10-20份；偶联剂：0.5-1份；催化剂：0.5-1份；丙酮：20-45份；甲苯：10-35份。3.根据权利要求1所述的光固化树脂，其特征在于，所述的丙烯酸树脂为纯丙烯酸树脂、聚醚类丙烯酸树脂和聚酯类丙烯酸树脂中的至少一种。4.根据权利要求1所述的光固化树脂，其特征在于，所述的环氧树脂为环氧树脂E-51和/或环氧树脂E-20。5.根据权利要求1所述的光固化树脂，其特征在于，所述的有机硅树脂为羟值4的甲基乙烯基硅油和/或羟值6的甲基乙烯基硅油。6.根据权利要求1所述的光固化树脂，其特征在于，所述的催化剂为叔胺和/或二月桂酸二丁基锡。7.一种光固化树脂的制备方法，其特征在于，其包括：1)将环氧树脂、丙烯酸树脂分别溶解于...
【专利技术属性】
技术研发人员：张宝华，黄成生，
申请(专利权)人：东莞市德聚胶接技术有限公司，
类型：发明
国别省市：广东,44