The invention discloses a method for preparing an anti rutting performance excellent road asphalt, the waste tire rubber powder after desulfurization of surface oxidation, plasma activation treatment, after gasoline activation treatment, improve the waste tire rubber modified asphalt high temperature performance and elastic recovery performance. The powder surface active group content of oxidized and first activated in improving physical blending and chemical reaction under the action of double, combined with high performance asphalt interface, improved asphalt cohesion and flexibility, to avoid the gasoline two activation brings softening lower point, also depends on the two gasoline once activated, elastic recovery performance, road performance has been greatly improved, anti rutting ability.
【技术实现步骤摘要】
一种抗车辙性能优异的路用胶粉沥青的制备方法
本专利技术涉及一种沥青路面材料的制备方法，具体涉及一种抗车辙性能优异的路用胶粉沥青的制备方法。
技术介绍
沥青路面是我国公路与城市道路的主要路面结构形式。随着国民经济的高速发展，交通密度和重型车辆日益增多，从而使沥青路面受到严峻考验，从经济环保的角度出发，国内外开展了利用废轮胎胶粉改性沥青应用于筑路的研究工作，具有更强的抗老化、抗疲劳、减少噪音、增大摩擦等优点，同时还具备低温抗裂性、高温稳定性、耐久性等特点。关于橡胶沥青的作用机理目前主要有3学说，即物理共混说、网络填充说以及化学共混说。沥青按三组分组成进行分析时，沥青中除了沥青质外，其他芳香芬等都是轻质组分，在制备橡胶沥青时，高温条件下，一部分轻质组分会被橡胶粉吸收，吸收了轻质组分的橡胶粉体积会膨胀，在其表面形成一层比较厚的凝胶层，这个过程中胶粉颗粒没有分解，并没有溶解在沥青中，仍然保持着原来的性质，由于轻质组分的减少，沥青变硬，且粘度变大。硫化胶粉中橡胶分子链已经交联成网络结构，流动性差，表面活性低，加工性能差，与基质沥青的相容性较差，使得胶粉在沥青中容易沉淀、离析，...
【技术保护点】
一种抗车辙性能优异的路用胶粉沥青的制备方法，其特征在于，将脱硫后的废轮胎胶粉进行表面氧化、低温等离子体活化处理后，之后经汽油活化处理，提高废轮胎胶粉改性沥青的高温性能和弹性恢复性能。
【技术特征摘要】
1.一种抗车辙性能优异的路用胶粉沥青的制备方法，其特征在于，将脱硫后的废轮胎胶粉进行表面氧化、低温等离子体活化处理后，之后经汽油活化处理，提高废轮胎胶粉改性沥青的高温性能和弹性恢复性能。2.根据权利要求书1所述的一种抗车辙性能优异的路用胶粉沥青的制备方法，其特征在于，具体步骤如下：（1）氧化改性：将80-100重量份经脱硫处理后的废轮胎胶粉置于反应瓶中，加入250-600份蒸馏水，充分搅拌使其混合均匀，加入20-40份氧化剂，在水浴锅中于45-80℃恒温条件下搅拌2-4小时，反应结束后进行抽滤洗涤，所得胶粉烘干至质量不再变化，制得氧化改性胶粉；（2）低温等离子体活化：将上述氧化改性胶粉均匀平铺在200目筛网上，水平放置于低温等离子体活化仪内腔中，抽真空至腔内气压真空度为30-60Pa，开启电源放电，控制腔内气压满足辉光放电，产生低温等离子体，活化2-8分钟；（3）二次活化：按照2-4:1的质量比向上述活化后的胶粉中注入常用汽油，常温下混合拌匀，用塑料袋将其密封，以减少汽油在空气中蒸发，在常温下充分融...
【专利技术属性】
技术研发人员：李国友，
申请(专利权)人：安徽中宏橡塑有限公司，
类型：发明
国别省市：安徽,34