The invention relates to a chiral poly (sebacic two diacylglycerols) preparation methods, including using chiral glycidyl as starting materials, preparation of chiral sebacic acid monoglycidyl ester, and then through the acid induced epoxy ring opening reaction for the preparation of chiral PSeD. The preparation method of the invention has the advantages of simple structure, low cost, chiral PSeD preparation is more regular, chains more closely than random PSeD crystallinity and mechanical strength of chiral PSeD has been greatly improved, the maximum load and elastic modulus after crystallization is 2 to 3 times random PSeD, to promote cell differentiation has obvious effect, has better application prospect.
【技术实现步骤摘要】
一种手性聚(癸二酰基甘油二酯)的制备方法
本专利技术属于聚酯材料领域，特别涉及一种手性聚(癸二酰基甘油二酯)的制备方法。
技术介绍
在新发展起来的聚酯材料中，聚癸二酸甘油酯[Poly(glycerolsebacate),PGS]是其中突出的代表之一。PGS聚酯材料出现于10多年前，由Wang课题组首先合成报道，是最早被引入组织工程领域的聚酯材料之一，PGS最初是为心血管组织工程设计的，因此在该领域首先获得了应用。而PGS本身也由于其诸多优良的特性，获得了持续广泛的研究关注，并且表现出了良好的发展和应用前景。近年来人们尝试通过对其进行修饰改性来提高其力学强度，如在PGS中添加柠檬酸、乙醇酸和一些无机纳米粒子来调节PGS的力学性能，显现出了不错的效果。通过研究物质材料的手性性质，利用不同手性材料的差异，可以研究发展生物相容性更高或者能够有效避免蛋白质或者细胞粘附的材料。但是目前，关于控制合成手性PGS尚未见到报道。
技术实现思路
本专利技术所要解决的技术问题是提供一种手性聚(癸二酰基甘油二酯)的制备方法，该方法简单，成本低，制备的手性PSeD结构更加规整，分子链排列更加紧...
【技术保护点】
一种手性聚(癸二酰基甘油二酯)的制备方法，包括：(1)将手性缩水甘油、三乙胺和甲苯于保护气氛保护的容器中混合，待温度降到0℃以下后，加入癸二酰氯保持温度搅拌反应5～10个小时；反应结束后将反应液抽滤，旋转蒸发除去溶剂，得到固体产物；然后将固体产物溶解，经过柱层析、重结晶得到手性癸二酰基缩水甘油酯；其中，癸二酰氯、手性缩水甘油和三乙胺的摩尔比为l:2‑3:4‑6；(2)将手性癸二酰基缩水甘油酯、癸二酸和四丁基溴化铵混合于有机溶剂中，90～150℃、保护气氛保护下搅拌反应5～30小时；反应结束后将反应液洗涤，除去溶剂，得到手性聚(癸二酰基甘油二酯)；其中，手性癸二酰基缩水甘油酯...
【技术特征摘要】
1.一种手性聚(癸二酰基甘油二酯)的制备方法，包括：(1)将手性缩水甘油、三乙胺和甲苯于保护气氛保护的容器中混合，待温度降到0℃以下后，加入癸二酰氯保持温度搅拌反应5～10个小时；反应结束后将反应液抽滤，旋转蒸发除去溶剂，得到固体产物；然后将固体产物溶解，经过柱层析、重结晶得到手性癸二酰基缩水甘油酯；其中，癸二酰氯、手性缩水甘油和三乙胺的摩尔比为l:2-3:4-6；(2)将手性癸二酰基缩水甘油酯、癸二酸和四丁基溴化铵混合于有机溶剂中，90～150℃、保护气氛保护下搅拌反应5～30小时；反应结束后将反应液洗涤，除去溶剂，得到手性聚(癸二酰基甘油二酯)；其中，手性癸二酰基缩水甘油酯和癸二酸的摩尔比为1:0.9-1.1。2.根据权利要求1所述的一种手性聚(癸二酰基甘油二酯)的制备方法，其特征在于：所述步骤(1)中的三乙胺经过氢氧化钠除水处理；甲苯经过钠丝除水处理。3.根据权利要求1所述的一种手性聚(癸二酰基甘油二酯)的制备方法，其特...