The present invention provides a method of using chemical to \oasis\ grass pulp fiber as raw materials in the preparation method, in particular: (1) take the hay or forage grass, mechanical crushing, spare; (2) the milled forage soaked, added to the cooking liquor, cooking for 9 hours in 6 95 100 C, the atmospheric conditions are short fiber; (3) short fiber filter after cooking, filter out short fiber; (4) the filtered short fiber acid to neutral, rub, then rinse with clean water; (5) the rinse fiber drying or drying; (6) using biochemical methods production wastewater treatment, discharge standards; the method can be applied to the largest pulp fiber production, easy operation, more economical.
【技术实现步骤摘要】
采用化学方法制取菌草浆纤维的方法
本专利技术属于一种采用化学方法制取纺织用浆纤维的方法，具体是利用绿洲一号巨菌草茎秆制取纺织用浆纤维的方法。
技术介绍
目前大多纺织用纤维的制取采用从竹子里提取，竹纤维是从自然生长的竹子中提取出的一种纤维素纤维，是继棉、麻、毛、丝之后的第五大天然纤维。竹纤维主要有竹原纤维、竹浆纤维、竹炭纤维几大类型。其中，竹原纤维是一种全新的天然纤维，是采用物理、化学相结合的方法制取的天然竹纤维。竹原纤维具有吸湿、透气、抗菌抑菌、除臭、防紫外线等良好的性能。迄今为止，竹纤维的生产基本上采用截段、分片、去青、去黄、蒸煮、压轧成竹丝束等工序，脱离不了先成竹片再成竹纤维束的工艺，其加工技术较落后，生产效率低下，加工设备功能单一，加工材料浪费严重，无法对整根竹子或竹边角料进行加工以实现高效规模化生产。而巨菌草，具体而言，是一种用于水土保持、防风固沙功能的“绿洲一号”菌草，其具有发达的根系能够用于沙漠地区的防风固沙，而且能够改善土壤特性，重要的是，其茎秆具有极快的生长速度，一年之内，在温度湿度适宜的情况下能够生长收割4-6茬，这种高产量的具有芦竹特性的菌草茎...
【技术保护点】
一种制取浆纤维的方法，其特征在于采用如下步骤：(一)取菌草干草或鲜草，将其机械粉碎，备用；(二)将粉碎好的草料浸湿，加入到蒸煮液中，在95‑100℃、常压条件下蒸煮6‑9小时，得到短纤维；(三)压滤蒸煮后得到的短纤维，滤出短纤维；(四)将滤出的短纤维酸洗至中性，揉搓，再用清水漂洗干净；(五)将漂洗干净的纤维晾干或烘干；(六)采用生化方法处理生产废水，达标排放。
【技术特征摘要】
1.一种制取浆纤维的方法，其特征在于采用如下步骤：(一)取菌草干草或鲜草，将其机械粉碎，备用；(二)将粉碎好的草料浸湿，加入到蒸煮液中，在95-100℃、常压条件下蒸煮6-9小时，得到短纤维；(三)压滤蒸煮后得到的短纤维，滤出短纤维；(四)将滤出的短纤维酸洗至中性，揉搓，再用清水漂洗干净；(五)将漂洗干净的纤维晾干或烘干；(六)采用生化方法处理生产废水，达标排放。2.如权利要求1所述的方法，其特征在于：步骤(二)中，所述浸湿的方法为：(1)取尿素溶于水中，在38-45℃下搅拌均匀，得到质量分数为1-3％的尿素水溶液；(2)将粉碎的草料浸于上述尿素水溶液中，浸泡2-5小时；(3)取出浸泡后的草料静置1-3小时，清水...