复合陶瓷粉体的酶催化凝胶反应合成方法技术

本发明专利技术属于无机非金属材料领域，涉及到多组元陶瓷复合粉体固相反应合成技术的改进。本发明专利技术的步骤是：配料－配制底物水溶液－加分散剂－球磨－加生物酶－干燥－煅烧。本发明专利技术所使用的所有原材料没有毒性，不会带来环境污染问题，而且价格较低。因此，本发明专利技术适用面广、成本低、操作简便、无环境污染、所得粉体质量高，适于工业化生产。（*该技术在2024年保护过期，可自由使用*）

Enzyme catalyzed gel reaction synthesis method of composite ceramic powder

The invention belongs to the field of inorganic non-metallic materials, and relates to the improvement of the solid phase reaction synthesis technology of a composite component ceramic composite powder. The steps of the invention are as follows: proportioning - preparing substrate water solution - adding powder - ball milling - adding biological enzyme - drying - calcining. All the raw materials used in the invention are not toxic, and can not bring environmental pollution problems, and the price is lower. Therefore, the invention has the advantages of wide application, low cost, simple operation, no environmental pollution and high quality of the obtained powder, and is suitable for industrial production.

【技术实现步骤摘要】

本专利技术属于无机非金属材料领域，涉及到多组元陶瓷复合粉体固相反应合成技术的改进。
技术介绍
陶瓷粉体的特性对特种陶瓷材料的制备工艺和微观结构有重要影响，继而对陶瓷部件的性能产生较大影响。因此，研究用先进的工艺方法制备高性能的陶瓷粉体一直是陶瓷材料发展的一个重要方面。目前传统的陶瓷粉体制备方法有固相法、液相法、气相法、机械法和溶剂蒸发法等，采用这些传统的方法制备陶瓷粉料通常会有粉料成分不均、合成温度高、工序复杂、设备要求高和粉料的纯度不高、粒度难以达到要求等问题。1989年法国的A.Douy和P.Odier提出了一种用聚丙稀酰胺液相凝胶法合成陶瓷氧化物粉体的办法(Mat.Res.Bull.，Vol.24，pp.1119-1126，1989，Printed in the USA，Pergamon Press plc.)，但此方法只能采用水溶性盐作为原料，成本较高，并有一定的环境污染，使其应用范围受到一定限制。后来陈大明等人提出了一种新的合成陶瓷复合粉体的方法——凝胶固相反应法(中国专利号99100590.2)。这种方法采用将水溶性有机单体(丙稀酰胺)和交联剂(N，N-亚甲基双丙烯酰本文档来自技高网...

【技术保护点】
一种复合陶瓷粉末的酶催化凝胶反应合成方法，其特征在于，该方法的操作步骤如下：（１）配料，按照所要制备的复合陶瓷粉末的预定配方配制陶瓷原料；（２）配制底物水溶液，在去离子水中加入０．２～５ｍｏｌ％的底物，并使其完全溶解，制得底 物的水溶液，其中底物为下列物质之一：尿素、内酯、甲酰胺、葡萄糖、淀粉；（３）加分散剂，将底物水溶液与陶瓷原料、分散剂混合，陶瓷原料的固相体积分数为２０ｖｏｌ％～６０ｖｏｌ％，分散剂为下列物质之一或几种物质的混合物：聚丙烯酸、聚甲基聚 丙烯酸氨、丙烯酸－丙烯酸脂二元共聚物、柠檬酸氨，分散剂的用量占陶瓷原料重量的０．５～３％；（４）...

【技术特征摘要】