The invention relates to a method for preparing perovskite ceramic powder, belonging to the field of preparing perovskite ceramic powder. During the preparation of perovskite ceramic powders by precipitation method, the solubility of the reactants in solution limits the production capacity of powders. The first step of the present invention, to include B (where B is one or more of Ti, Zr and Sn elements in the B) completely precipitated adding excess precipitant solution, after the separation of the precipitation form suspension and preheating to 60-95 DEG C in the solvent dispersion; the second step is added to the heated suspension contains A (A Mg, Ca, Ba and Pb elements in one or several) hydroxide or A containing salt and precipitant, at a temperature of 60-95 DEG C ultrasonic treatment for 10 240Min, the powder are filtered, washed and dried, greatly expand the selection range of solvent.
【技术实现步骤摘要】
本专利技术属于制备钙钛矿陶瓷粉体的领域。本专利技术涉及一种制备单一的或均匀的复合固溶体钙钛矿陶瓷粉体的方法。具体地，本专利技术涉及一种制备钙钛矿陶瓷粉体的超声化学方法。更具体地，本专利技术涉及一种采用两步法，在超声波辐射条件下制备钙钛矿陶瓷粉体的方法。
技术介绍
以钛酸钡为代表的钙钛矿陶瓷粉体是目前国内外应用最广泛的制备电子陶瓷的原料，钙钛矿陶瓷粉体通过掺杂及其它手段可以获得具有合适的介电常数，良好的铁电、压电、耐压及绝缘性能，主要用来制造高电容积层电容器、多层积片、各种传感器、半导体材料和敏感原件，具有重要的商业价值。由于钙钛矿电子陶瓷是以钙钛矿陶瓷粉体为原料经成型和煅烧形成陶瓷体而制备得到的，因此，粉体的质量将直接影响产品的质量。近年来，电子元器件正在向小型化、多功能化、高性能化、集成化发展，电子工业对具有钙钛矿结构的粉体的纯度、颗粒尺寸、成型以及烧结特性提出了更高的要求，因此研制纯度高、粒径小、粒度分布窄、结晶性优良、颗粒形貌规整的电子陶瓷粉体具有广阔的应用前景和重要的战略意义。传统的固相法制备的粉体粒径较大，远不能满足电子元器件小型化，多功能化的发展要...
【技术保护点】
一种制备钙钛矿陶瓷粉体的方法，其特征在于，包括以下步骤：第一步，向包含Ｂ的溶液中加入过量沉淀剂使Ｂ完全沉淀，分离后将所得沉淀在溶剂中分散形成悬浊液并预热至６０－９５℃；第二步，向上述预热后的悬浊液中加入包含Ａ的氢氧化物或包含 Ａ的盐及沉淀剂，在６０－９５℃的温度下超声处理１０－２４０ｍｉｎ，经过滤、洗涤、干燥后得到粉体；其中Ａ为Ｍｇ、Ｃａ、Ｓｒ、Ｂａ和Ｐｂ元素中的一种或几种；Ｂ为Ｔｉ、Ｚｒ和Ｓｎ元素中的一种或几种；包含Ａ离子与Ｂ离子的摩尔比为０．９－１． ６；Ａ离子在反应溶液中的浓度为０．０１－１ｍｏｌ／Ｌ；超声波强度为２５－１５０Ｗ／ｃｍ↑［２］。
【技术特征摘要】