The present invention provides a method of hydrothermal synthesis of strontium titanate ceramic powder, the titanium containing compounds added to the aqueous solution of sodium hydroxide, hydrolysis, separation and washing to obtain hydrated titanium oxide, and then according to stoichiometry hydrated titanium oxide and strontium compound in alkaline solution by mixing and refluxing at atmospheric pressure the reaction under the protection of inert gas, then the reaction mixture solution after separation, washing and drying to obtain the strontium titanate ceramic powder. The strontium titanate ceramic powder prepared by the invention has the advantages of uniform particle size, little impurity, simple process, low cost and easy realization of large-scale industrial production.
【技术实现步骤摘要】
本专利技术涉及多功能电子陶瓷材料——钛酸盐陶瓷粉体的制备方法，尤其涉及一种利用。
技术介绍
钙钛矿型钛酸盐(主要为BaTiO3、SrTiO3、PbTiO3、CaTiO3)是一种具有较高介电常数的电介质材料、光电材料，具有高容量、高色散频率、低介电耗损、低温度系数的特点。单一钛酸盐材料具有混合电子和离子电导，使得它在高温超导薄膜、催化、高温固体氧化物燃料电池电极材料、电化学传感器、多种氧化物薄膜衬底材料、特殊光学窗口及高质量的溅射靶材等方面应用广泛。掺杂或复合钛酸盐陶瓷材料具有多功能的特性，制造的产品可以分别具有压电、铁电、导电、半导体、磁性等或具有高强、高韧，高硬、耐磨、耐腐蚀、耐高温、高热导、绝热或良好生物相容性等特点，是一类先进的多功能陶瓷材料。钛酸盐在电子元器件方面用途广泛，被誉为“电子工业的支柱”。如用于制造芯片的陶瓷绝缘材料、陶瓷基板材料、陶瓷封装材料以及用于制造电子器件的电容器陶瓷、压电陶瓷、铁氧体磁性材料等。对钛酸盐进行掺杂和复合还可以得到用于制造介质谐振器，微波集成电路基片、元件等的微波陶瓷。钛酸盐基陶瓷还可用于制造对温度、压力、湿度、气氛、光等...
【技术保护点】
一种钛酸锶ＳｒＴｉＯ↓［３］粉体的制备方法，包括以下次序的工艺步骤：①在强烈搅拌下，将含钛化合物加至氢氧化钠水溶液中，水解、分离、洗涤得到水合钛氧化物ＴｉＯ↓［２］.ｎＨ↓［２］Ｏ；②将水合钛氧化物ＴｉＯ↓［２］.ｎＨ↓［２］Ｏ、含锶化合物在碱溶液中混合，搅拌并加热；③在惰性气体保护下，常压水热回流反应１－１０小时；④分离混合液、并洗涤、干燥分离物得钛酸锶粉体。
【技术特征摘要】
【专利技术属性】
技术研发人员：贾永忠，景燕，金山，
申请(专利权)人：中国科学院青海盐湖研究所，
类型：发明
国别省市：63[中国|青海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。