The invention discloses a low consumption of iron and steel converter steelmaking method, including feeding, blowing, deoxidizing and alloying, tapping, in the feeding process, hot metal temperature more than 1250 DEG C, molten iron in S is less than or equal to 0.050%, into the furnace scrap steel, scrap steel and billet head more than iron; hot metal temperature less than 1250 degrees Celsius, the molten iron in S is more than 0.050%, the proportion of scrap steel is greater than iron into the furnace billet head, waste steel and iron; if S is greater than or equal to 0.065%, into the furnace for scrap iron. The converter steelmaking method with the above step parameters greatly reduces the consumption of steel material, reduces the cost and improves the economic benefit.
【技术实现步骤摘要】
本专利技术涉及一种转炉炼钢的方法。
技术介绍
钢铁料消耗是转炉炼钢生产中的一项重要指标，亦是炼钢厂工艺装备、工艺操作和各项管理水平的综合体现，且占炼钢生产总成本80％左右。组织钢铁料消耗攻关，就是将影响钢铁料消耗的各项因素逐项分析，查找可改善的因素，达到钢铁料消耗攻关的目的。钢铁消耗增大的主要原因有：1铁水质量差(带渣量大，S、P偏高，Si、S波动大)，2石灰质量差(活性度低、粉末多、有效CaO过低)。
技术实现思路
有鉴于此，本专利技术提供一种低钢铁料消耗的转炉炼钢方法，用于降低转炉炼钢时钢铁料的消耗。为解决以上技术问题，本专利技术的技术方案为：一种低钢铁料消耗的转炉炼钢方法，包括加料、吹炼、脱氧合金化、出钢，在加料过程中，入炉铁水温度≥1250℃，铁水中S≤0.050％，入炉废钢中钢坯头、废钢材之和的比例大于生铁；入炉铁水温度＜1250℃，铁水中S＞0.050％，入炉废钢中生铁比例大于钢坯头、废钢材之和；若铁水中S≥0.065％，入炉废钢全为生铁。作为一种改进，在吹炼过程的前、中期分批加入球团矿；吹炼后期禁止加入球团矿。在铁水S不高的情况下，通过增加球团矿用量，...
【技术保护点】
一种低钢铁料消耗的转炉炼钢方法，包括加料、吹炼、脱氧合金化、出钢，其特征在于：在加料过程中，入炉铁水温度≥1250℃，铁水中S≤0.050％，入炉废钢中钢坯头、废钢材之和的比例大于生铁；入炉铁水温度＜1250℃，铁水中S＞0.050％，入炉废钢中生铁比例大于钢坯头、废钢材之和；若铁水中S≥0.065％，入炉废钢全为生铁。
【技术特征摘要】
1.一种低钢铁料消耗的转炉炼钢方法，包括加料、吹炼、脱氧合金化、出钢，其特征在于：在加料过程中，入炉铁水温度≥1250℃，铁水中S≤0.050％，入炉废钢中钢坯头、废钢材之和的比例大于生铁；入炉铁水温度＜1250℃，铁水中S＞0.050％，入炉废钢中生铁比例大于钢坯头、废钢材之和；若铁水中S≥0.065％，入炉废钢全为生铁。2.根据权利要求1所述的一种低钢铁料消耗的转炉炼钢方法，其特征在于：在吹炼过程的前、中期分批加入球团矿；吹炼后期禁止加入球团矿。3.根据权利要求1所述的一种低钢铁料消耗的转炉炼钢方法，其特征在于：在吹炼过程中，利用0.85MPa氧气进行大于60秒深吹。4.根据权利要求1所述的一种低钢铁料消耗的转炉炼钢方法，其特征在于：在吹炼时加入活性石灰；吹炼前期加入活性石灰总量的2/3，吹炼后期加入1/3。5.根据权利要求4所述的一种低钢铁料消耗的...
【专利技术属性】
技术研发人员：刘德斌，岑明安，张华，税宗鲜，陈劲松，胡科红，
申请(专利权)人：云南德胜钢铁有限公司，
类型：发明
国别省市：云南;53