The invention relates to a method for preparing titanium carbide powder. Method for preparing submicron TiC powder provided by the invention is: the particle size less than 1 mu m titanium dioxide with pressure of 0.5 ~ 0.8MPa air airflow crusher, collected particle size is 0.2 ~ 0.5 micron titanium dioxide; titanium dioxide and carbon black will be obtained by the steps of carbon black and titanium dioxide as the proportion of 0.44-0.45: 1 mixed by low-temperature vacuum carbonization preparation of submicron, namely titanium carbide powder particle size less than 1 micron; parameters of low temperature vacuum carbonization is said: at the end of the vacuum degree of vacuum carbonization is less than 10Pa, the temperature is 1350~1450 DEG C, the holding time is 7~13 hours. The method has the advantages of short flow, easy operation and low investment.
【技术实现步骤摘要】
本专利技术涉及碳化钛粉末的制备方法。
技术介绍
TiC显微硬度为3200公斤/厘米2,是难熔金属碳化物中最高的。由于其高的显微硬度,在硬质合金中得到了广泛的应用。其主要应用领域有两个1.作为硬质相与粘结相以及其他添加剂湿磨混合通过烧结制备钢结合金,钢结合金主要应用于耐磨零件、耐蚀零件以及某些特殊刀具;2.作为溶剂在高温下将钨、钽等溶质原子固溶形成复合碳化物,这些复合碳化物与碳化钨、粘结剂及其他添加剂湿磨混合通过烧结用于制备硬质合金刀片。由于应用要求的提高,硬质合金的金相组织须更加均勻,更加细小。为了得到金相组织更加均勻和细小的硬质合金,作为其中的组成成分之一的TiC也必须更加细小和均勻。制备TiC粉末的传统方法是将普通TiO2与固体碳球磨混合、碳管炉一次碳化而成,此方法碳化温度较高(一般需要1800 2000°C )、碳化时间较长,粉末粒度一般为3 5 μ m左右,难以满足硬质合金越来越高的要求。亚微米材料是指粒度直径为IOOnm ~ l.Oym的材料。国内外对制备细颗粒TiC的报道较少,也主要集中在气相碳化、利用TiCl4进行碳化制备TiC,这些方法均存在成本高、难以实现工业化等缺点。
技术实现思路
本专利技术的目的是提供一种制备亚微米TiC粉末的方法。本专利技术提供的制备亚微米TiC粉末的方法是1)将粒度小于1 μ m钛白粉用压力为0. 5 0. SMPa的气流进行气流破碎,收集得到粒度为0. 2 0. 5微米钛白粉;2)将上述步骤获得的钛白粉与碳黑按碳黑与钛白粉的比例为0.44-0. 45 1混合均勻,通过低温真空碳化制备亚微米,即粒度小于1微米 ...
【技术保护点】
1.一种亚微米TiC粉末的制备方法,包括如下步骤:1)将粒度小于1微米的钛白粉经气流压力为0.5~0.8MPa的气流进行气流破碎,收集得到粒度为0.2~0.5微米的TiO2;2)将上述步骤获得的钛白粉与碳黑按碳黑与钛白粉的比例为0.44-0.45∶1混合均匀,通过低温真空碳化制备亚微米,即粒度小于1微米的碳化钛粉末;所说的低温真空碳化的参数条件是:真空碳化结束时真空度为小于10Pa,碳化温度为1350~1450℃,保温时间为7~13小时。
【技术特征摘要】
【专利技术属性】
技术研发人员:郭伟,
申请(专利权)人:长沙伟徽高科技新材料股份有限公司,
类型:发明
国别省市:43
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。