一种新型铸造型砂及其制备方法技术

一种铸造型砂，由以下重量份数原料组成：石英砂65‑80份、重烧镁砂30‑40份、刚玉砂30‑40份、高岭土20‑30份、粘土40‑60份、碳酸钠6‑15份、玻璃纤维5‑9份、生活垃圾灰渣40‑60份、粉煤灰8‑13份、轻烧粉20‑30份、呋喃树脂6‑9份，煤粉11‑21份、水30‑50份。本发明专利技术的有益效果为：（1）该铸造型砂没有添加煤粉，避免了煤粉粘土砂对环境的污染；（2）本发明专利技术各成分合理的配比，使得制备的型砂质量优异，采用该型砂生产的铸件表面光滑，且生产该型砂的方法成本低。

A new type of casting sand and its preparation method

A sand casting, which consists of the following parts by weight of raw materials: quartz sand 65 80 copies, 40 copies, 30 burned magnesia corundum 30 40 copies, 30 copies, 20 kaolin clay 40 60 copies, 15 copies, 6 sodium carbonate glass fiber 5 9, MSW 40 60, fly ash 8 13 copies, 30 copies of light burning powder 20, furan resin 6 9 copies, 21 copies, 11 coal water 30 50. The beneficial effects of the invention are: (1) the casting sand without adding pulverized coal, coal and clay sand to avoid the pollution to the environment; (2) the composition of the invention reasonable ratio, the quality of sand preparation makes excellent use of the casting surface sand production method and the production cost is smooth, the sand is low.

【技术实现步骤摘要】
一种新型铸造型砂及其制备方法
本专利技术涉及铸造
，具体涉及一种新型铸造型砂及其制备方法。
技术介绍
型砂在铸造中用来造型的材料。型砂一般由铸造用原砂、型砂粘结剂和辅加物等造型材料按一定的比例混合而成。型砂按所用粘结剂不同，可分为粘土砂、水玻璃砂、水泥砂、树脂砂等。以粘土砂、水玻璃砂及树脂砂用的最多。在铸造过程中，将会产生大量的废弃旧砂，如果不能对其进行循环利用，将会造成大量的浪费及对环境的污染。同时，现有技术中一般使用的煤粉粘土湿型砂，但是煤粉最终容易对环境产生污染。
技术实现思路
本专利技术的目的是为了克服现有技术中的不足，提供一种新型铸造型砂及其制备方法。为解决上述技术问题，本专利技术的技术方案为：一种新型铸造型砂，由以下重量份数原料组成：硅砂120-140份、锆砂11-18份、方解石砂55-65份，滑石粉9-15份，碳质砂9-15份，膨润土9-12份，草木灰6-11份，秸秆粉末4-7份，尾矿渣微粉2-6份、耐火熟料6-9份、水12-16份。进一步的，所述的耐火熟料为质量比为75%的铝矾土和25%的煤矸石混合物。一种制备上述型砂的方法为，包括以下步骤：（1）将上述重量份数的草本文档来自技高网...

【技术保护点】
一种新型铸造型砂，其特征在于：由以下重量份数原料组成：硅砂120‑140份、锆砂11‑18份、方解石砂55‑65份，滑石粉9‑15份，碳质砂9‑15份，膨润土9‑12份，草木灰6‑11份，秸秆粉末4‑7份，尾矿渣微粉2‑6份、耐火熟料6‑9份、水12‑16份。

【技术特征摘要】
1.一种新型铸造型砂，其特征在于：由以下重量份数原料组成：硅砂120-140份、锆砂11-18份、方解石砂55-65份，滑石粉9-15份，碳质砂9-15份，膨润土9-12份，草木灰6-11份，秸秆粉末4-7份，尾矿渣微粉2-6份、耐火熟料6-9份、水12-16份。2.根据权利要求1所述的一种新型铸造型砂，其特征在于：所述的耐火熟料为质量比为75%的铝矾土和25%的煤矸石混合物。3.一种制...

【专利技术属性】
技术研发人员：鲁茂波，
申请(专利权)人：东风精密铸造安徽有限公司，
类型：发明
国别省市：安徽,34