A kind of environment-friendly casting sand, which consists of the following parts by weight: 70 raw quartz sand 88, calcined 30 40, fused sand 30 40 copies, 12 copies of bentonite 9, corn flour 6 9 copies, 3 copies of 7 sawing processing sawdust, rice bran powder 2 5 copies, 65 copies of 45 water, light burning powder 20 30, Magnesium Oxide 9 14 copies, 14 copies of 5 insulation covering agent. The beneficial effects of the invention are: (1) the molding sand is environment-friendly and non volatile toxic gas, and has no harmful effects on human body and environment; (2) the cost of the molding sand is low, and the high temperature resistant performance is excellent, so the cracks and shrinkage holes of the final casting surface will not be made.
【技术实现步骤摘要】
一种环保型铸造型砂
本专利技术涉及铸造
,具体涉及一种环保型铸造型砂。
技术介绍
铸造是将金属熔炼成符合一定要求的液体并浇进铸型里,经冷却凝固、清整处理后得到有预定形状、尺寸和性能的铸件的工艺过程。铸造毛坯因近乎成形,而达到免机械加工或少量加工的目的降低了成本并在一定程度上减少了制作时间.铸造是现代装置制造工业的基础工艺之一。型砂,主要有砂型铸造和特种铸造2大类。普通砂型铸造,利用砂作为铸模材料,又称砂铸,翻砂,包括湿砂型、干砂型和化学硬化砂型3类,但并非所有砂均可用以铸造。好处是成本较低,因为铸模所使用的沙可重复使用;缺点是铸模制作耗时,铸模本身不能被重复使用,须破坏后才能取得成品。特种铸造,按造型材料又可分为以天然矿产砂石为主要造型材料的特种铸造(如熔模铸造、泥型铸造、壳型铸造、负压铸造、实型铸造、陶瓷型铸造等)和以金属为主要铸型材料的特种铸造(如金属型铸造、压力铸造、连续铸造、低压铸造、离心铸造等)两类。铸件在生产过程中经常会发生各种不同的铸造缺陷,如裂纹、气孔、砂眼、缩孔等,随着型砂原材料价格的增长,型砂铸造的成本也越来越高。
技术实现思路
本专利技术的目的是为了克服现有技术中的不足,提供一种环保型铸造型砂。为解决上述技术问题,本专利技术的技术方案为:一种环保型铸造型砂,由以下重量份数原料组成:石英砂70-88份,重烧镁砂30-40份,电熔皮砂30-40份,膨润土9-12份,玉米面粉6-9份,锯加工木屑3-7份,稻糠粉2-5份,水45-65份,轻烧粉20-30份,氧化镁9-14份,保温覆盖剂5-14份。优选地,由以下重量份数原料组成:石英砂70份 ...
【技术保护点】
一种环保型铸造型砂,其特征在于:由以下重量份数原料组成:石英砂70‑88份,重烧镁砂30‑40份,电熔皮砂30‑40份,膨润土9‑12份,玉米面粉6‑9份,锯加工木屑3‑7份,稻糠粉2‑5份,水45‑65份,轻烧粉20‑30份,氧化镁9‑14份,保温覆盖剂5‑14份。
【技术特征摘要】
1.一种环保型铸造型砂,其特征在于:由以下重量份数原料组成:石英砂70-88份,重烧镁砂30-40份,电熔皮砂30-40份,膨润土9-12份,玉米面粉6-9份,锯加工木屑3-7份,稻糠粉2-5份,水45-65份,轻烧粉20-30份,氧化镁9-14份,保温覆盖剂5-14份。2.根据权利要求1所述的一种环保型铸造型砂,其特征在于:由以下重量份数原料组成:石英砂70份,重烧镁砂30份,电熔皮砂30份,膨润土9份,玉米面粉6份,锯加工木屑3份,稻糠粉2份,水45份,轻烧粉20份,氧化镁9份,保温覆盖剂5份。3.根据权利要求1所述的一种环保...