The present invention is a doped graphene conductive two-component silicone sealant and preparation method thereof, which is composed of two components: one is the base component paste by liquid vinyl silicone rubber, reinforcing agent, conductive filler, catalyst, inhibitor and diluent, component two crosslinking agent. The two components are weighed according to the proportion and put into the container and can be used after mixing evenly. The sealant can be cured at room temperature and also can be cured by heating. It is widely used in many fields. It has high conductivity and excellent mechanical properties.
【技术实现步骤摘要】
能够掺杂石墨烯的双组分导电有机硅密封胶及其制备方法
本专利技术是一种能够掺杂石墨烯的双组分导电有机硅密封胶及其制备方法，属于高分子材料及其生产
技术介绍
现代武器装备大量应用电子产品，同时不断地向高速化、集成化、复杂化发展，其电路本身将产生大量各种频率的电磁辐射信号，造成电子设备间发生电磁干扰现象，从而对人体和武器装备产生重大影响；为了消除电子设备间的电磁干扰、消除静电、密封防腐蚀及减振，就需要采用弹性的导电密封胶对电子设备进行密封。高导电有机硅密封胶是一类新型功能有机硅密封材料，除了具有通常有机硅密封胶优异的耐高低温性能外，还有很高的导电性，已经应用于航空和航天飞行器、核电和电子电器等领域，以实现消除静电、电磁屏蔽及密封。当前高导电有机硅密封胶仍存在以下问题：(1)高导电有机硅密封胶按其固化方式分为：缩合型高导电有机硅密封胶和加成型高导电有机硅密封胶。缩合型高导电有机硅密封胶(如专利CN103351839A和专利CN1775862A)依赖空气中的水分固化，因此，存在以下缺点：一是固化速度受到空气温度和湿度双重影响，对现场施工条件有一定的要求；二是加温对...
【技术保护点】
一种能够掺杂石墨烯的双组分导电有机硅密封胶，其特征在于：该密封剂是由两个组分构成，其中：组分一的组成原料及质量份数为：液体乙烯基聚硅氧烷生胶100，补强剂8～25，导电填料200～500，催化剂0.01～2，抑制剂0.05～2，稀释剂0～5；组分二的组成原料是交联剂，组分一和组分二的质量比为100∶0.4～2.0；所述液体乙烯基聚硅氧烷生胶为乙烯基聚二甲基硅氧烷、乙烯基聚甲基苯基硅氧烷或乙烯基聚甲基三氟丙基硅氧烷，生胶粘度为1000mPa·s～20000mPa·s；所述补强剂为沉淀法白炭黑、气相法白炭黑、硅烷改性沉淀法白炭黑、硅烷改性气相法白炭黑或石墨烯中的一种或两种混合物...
【技术特征摘要】
1.一种能够掺杂石墨烯的双组分导电有机硅密封胶，其特征在于：该密封剂是由两个组分构成，其中：组分一的组成原料及质量份数为：液体乙烯基聚硅氧烷生胶100，补强剂8～25，导电填料200～500，催化剂0.01～2，抑制剂0.05～2，稀释剂0～5；组分二的组成原料是交联剂，组分一和组分二的质量比为100∶0.4～2.0；所述液体乙烯基聚硅氧烷生胶为乙烯基聚二甲基硅氧烷、乙烯基聚甲基苯基硅氧烷或乙烯基聚甲基三氟丙基硅氧烷，生胶粘度为1000mPa·s～20000mPa·s；所述补强剂为沉淀法白炭黑、气相法白炭黑、硅烷改性沉淀法白炭黑、硅烷改性气相法白炭黑或石墨烯中的一种或两种混合物；所述导电填料为银粉、镀银铜粉、镀银铝粉、镀...
【专利技术属性】
技术研发人员：范召东，郑付来，任河，刘梅，孙全吉，