The invention discloses a grid PET double-sided tape and its production process, the adhesive tape comprising a PET substrate, PET substrate in two surfaces are attached with increasing agent, in increasing agent evenly coated with a layer of adhesive layer, the adhesive layer is adhered with grid release paper. The advantages of the invention of the double-sided tape grid PET on PET substrate on the two surfaces are attached with increasing agent, it can significantly improve the adhesive layer on the PET substrate adhesion, adhesive tape stripping for better items, to avoid the residue, and the double-sided adhesive belt can tear off repeated use; in addition, the production process is simple and feasible, with excellent marketing application.
【技术实现步骤摘要】
网格PET双面胶带及其生产工艺
本专利技术涉及一种胶带，具体涉及一种网格PET双面胶带及其生产工艺。
技术介绍
双面胶带一般是由基材及涂布在基材的两个表面上的胶黏剂构成，胶带能够附着在物体表面起到粘接作用。根据基材划分，胶带可分为BOPP胶带、PET胶带、布基胶带、牛皮纸胶带、美纹纸胶带、纤维胶带、PVC胶带、PE泡棉胶带等；根据应用范围划分可分为警示胶带、地毯胶带、电工胶带、保护膜纸胶、缠绕膜胶带、封箱胶带、模块胶带等；根据市场普及率划分可分为普通胶带、特种胶带；根据应用环境温度划分可分为低温胶带、常温胶带、高温胶带。采用PET作为基材制成的双面胶带，简称为“PET双面胶带”，它是由PET双面涂布丙烯酸胶制成，胶带颜色一般为透明和黑色两种，少见的还包括绿色的PET双面胶带。常见厚度规格为：0.05-0.2MM，具有良好尺寸稳定性、热稳定性、化学稳定性，易模切加工，对塑胶、橡胶、铭牌均有良好的粘性，能适用于更宽的温度范围和恶劣环境：长期耐温100-120℃，短期耐温可达140-200℃。但是，目前市场上的PET胶带存在基材与胶黏剂之间的粘着强度不高的问题，导致产品...
【技术保护点】
网格PET双面胶带，其特征在于，包括PET基材、在PET基材的两个表面上均附着有增着剂、在增着剂上均匀涂布一层胶黏剂层，所述胶黏剂层上贴合有网格离型纸。
【技术特征摘要】
1.网格PET双面胶带，其特征在于，包括PET基材、在PET基材的两个表面上均附着有增着剂、在增着剂上均匀涂布一层胶黏剂层，所述胶黏剂层上贴合有网格离型纸。2.根据权利要求1所述的网格PET双面胶带，其特征在于，增着剂的制备方法为：将松香液分散于溶剂中，边搅拌边向其中滴加甘油，所述溶剂为醇类溶剂；所述松香液与甘油的质量比为3~5:1。3.根据权利要求1所述的网格PET双面胶带，其特征在于，所述PET基材的厚度为3~15μm。4.根据权利要求1所述的网格PET双面胶带，其特征在于，所述胶黏剂层包括如下重量份的各组分：丙烯酸15~30份、甲基丙烯酸甲酯10~25份、环氧树脂5~10份、乙酸乙酯8~15份、聚二甲基硅氧烷5~8份、氯化石蜡8~12份、芳香烃1~10份以及过氧化苯甲酰0.5~3份。5.根据权利要求4所述的网格PET双面胶带，其特征在于，所述芳香烃为甲苯或二甲苯。6.根据权利要求4所述的网格PET双面胶带，其特征在于，所述胶黏剂层的厚度为0.5~3μm。7.根据权利要求4所...
【专利技术属性】
技术研发人员：乐寿勇，
申请(专利权)人：江苏斯瑞达新材料科技有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。