The invention discloses an oil-free scroll vacuum pump Aluminum Alloy static plate manufacturing process, including cutting, sandblasting, lubrication and forging extrusion, solid solution and aging treatment process; forming steps for the extrusion lubrication and forging: heating to 220 - 10 DEG C, the blank surface coating the polymer lubricant, then the blank is heated to 515 + 5 DEG C, again oily coated on the surface of graphite, placed into 220 + 10 DEG C one-time extrusion die cavity. The product produced by the invention has the advantages of high internal organization density, good mechanical performance, high yield, long die life, high material utilization rate, high production efficiency, low cost and short production cycle.
【技术实现步骤摘要】
涡旋式无油真空泵铝合金静盘制造工艺
本专利技术属于锻造成形
，具体涉及一种医疗设备涡旋式无油真空泵铝合金静盘制造工艺。
技术介绍
医疗设备涡旋式无油真空泵，具有容积效率高、运转平稳、噪音低、振动低、零部件少、可靠性高等技术优点，铝合金涡旋静盘在涡旋式无油真空泵中属于关键零部件，产品质量好差直接影响涡旋式无油真空泵的整体质量。现有技术是采用铝合金棒材直接机加工的方法生产而成，由于母材直接切削加工，金属内部组织疏松、密度低、抗冲击力低，采用铝合金棒材直接切削加工的方法生产而成的涡旋式真空泵铝合金静盘机械性能不能满足整体产品设计和使用要求，且浪费铝合金材料，加工成本高，生产周期长。国内现有涡旋盘上的渐开线卷体都是采用压力铸造加工而成。中国专利CN1799765A公开了一种涡旋盘温挤压成形方法，是将铝合金坯料加热至450-500℃，然后取出已加热的铝合金坯料，在3-5S之内作润滑处理后即置入模腔内一次性挤压成形，取出成形的涡旋盘置放到165～180℃的回火炉中作8-10h的人工时效处理。其温挤加热之前没有涂覆石墨保护层，加热温度450-500℃表面易氧化，坯料润滑是...
【技术保护点】
涡旋式无油真空泵铝合金静盘制造工艺，其特征在于，所述制造工艺包括下料、喷砂、润滑和锻挤成形、固溶及时效处理工艺步骤；其中所述的润滑和锻挤成形步骤为：将坯料加热到220±10℃，在坯料表面涂覆高分子润滑剂，然后将坯料加热到515±5℃，再次进行表面涂覆油性石墨后，放置入220±10℃的模腔内一次性挤压成形。
【技术特征摘要】
1.涡旋式无油真空泵铝合金静盘制造工艺，其特征在于，所述制造工艺包括下料、喷砂、润滑和锻挤成形、固溶及时效处理工艺步骤；其中所述的润滑和锻挤成形步骤为：将坯料加热到220±10℃，在坯料表面涂覆高分子润滑剂，然后将坯料加热到515±5℃，再次进行表面涂覆油...
【专利技术属性】
技术研发人员：张太良，练强，姚鹏程，
申请(专利权)人：江苏威鹰机械有限公司，
类型：发明
国别省市：江苏,32