一种用于乙烯聚合的催化剂组分的制备方法技术
Method for preparing catalyst component for ethylene polymerization
The invention provides a method for preparing ethylene polymerization catalyst component comprises a magnesium compound dissolved in the solvent, and aromatic hydrocarbon based solvent system containing organic epoxy compound and organic phosphorus compounds, the formation of homogeneous solution, co existed in separating assistant and whisker conditions. Adding titanium compounds, reactive precipitation of the catalyst component. By the invention, a spherical or nearly spherical catalyst component with higher pore volume and specific surface area can be obtained, and the catalyst has excellent catalytic activity and stability.
【技术实现步骤摘要】
一种用于乙烯聚合的催化剂组分的制备方法
本专利技术涉及石油化工领域。具体涉及一种用于乙烯聚合的催化剂组分的制备方法及其产品和应用。
技术介绍
自上世纪50年代初，Ziegler-Natta先后通过钛系催化剂的低压聚合得到聚乙烯和聚丙烯以来，经过多年的发展，Ziegler-Natta型烯烃聚合催化剂在活性、氢调敏感度、等规度、共聚能力等方面已经取得了突破。在此基础之上，研究人员进一步认识到Ziegler-Natta型烯烃聚合催化剂的颗粒形态(包括粒度和形貌结构)同样是一个需要精确控制的方面，因此成为了近年来的一个研究热点。Ziegler-Natta型烯烃聚合催化剂粒子具有能把它们的形貌复制给其所制备聚烯烃粉料颗粒的特殊能力。如球形催化剂粒子通常生成球形的粉料颗粒，如高孔容催化剂粒子通常生成高孔容的粉料颗粒。而催化剂物理结构的改变，往往也会对催化剂性能带来明显的影响。例如，催化剂高孔容可以改善聚合过程中单体的扩散速率，进而提高催化剂的活性表现。但每一类催化剂，其成型机理又基本限定了催化剂成品的这些物理结构，并不容易随意改变。溶解析出型催化剂的代表，N系聚丙烯催化剂是由...
【技术保护点】
一种用于乙烯聚合的催化剂组分的制备方法，包括：将镁化合物溶解于以芳烃为基础溶剂、并含有机环氧化合物和有机磷化合物的溶剂体系中，形成均匀溶液后，在助析出剂和晶须共同存在的条件下，加入钛化合物，反应后析出，得到所述催化剂组分。
【技术特征摘要】
1.一种用于乙烯聚合的催化剂组分的制备方法，包括：将镁化合物溶解于以芳烃为基础溶剂、并含有机环氧化合物和有机磷化合物的溶剂体系中，形成均匀溶液后，在助析出剂和晶须共同存在的条件下，加入钛化合物，反应后析出，得到所述催化剂组分。2.根据权利要求1所述的制备方法，其特征在于，所述晶须为无机晶须，优选为硫酸镁晶须、碳化硅晶须和氧化铝晶须中的至少一种。3.根据权利要求1或2所述的制备方法，其特征在于，所述助析出剂包括有机酸酐、有机酸和有机酮中的至少一种，优选为乙酸酐、邻苯二甲酸酐、丁二酸酐、顺丁烯二酸酐、醋酸、丙酸、丁酸、丙烯酸、甲基丙烯酸、丙酮、甲乙酮和二苯酮中的至少一种。4.根据权利要求1-3中任一项所述的制备方法，其特征在于，基于每摩尔镁化合物计，有机环氧化合物为0.2-10mol，有机磷化合物为0.1-3mol，助析出剂为0.05-1.0mol，钛化合物为0.5-...