钢丝芳纶复合帘线制造技术

本发明专利技术公开了一种钢丝芳纶复合帘线，包括芳纶芯和外层金属，芳纶芯包括多根捻合在一起的芳纶线，芳纶线的断裂伸长率为2.5~4%，外层金属包括多根面线钢丝，面线钢丝的断裂伸长率为2.5~4%，外层金属缠绕在芳纶芯的外层，两者捻合在一起，面线钢丝的捻距为8~18mm。本发明专利技术的钢丝芳纶复合帘线的强度高、质量轻，增加了帘线的刚度，可以承受更高的断裂强度，且提高了钢丝和橡胶之间的粘合性能以及帘线的疲劳性能。

Steel wire aramid composite cord

The invention discloses a steel complex aramid cord, including aramid core and outer metal, aramid core includes a plurality of twisted together the aramid cord elongation of aramid cord for 2.5~4%, including a plurality of surface layer of metal wire line, elongation of wire surface is 2.5~4%, the outer metal winding in the outer layer of aramid core, two twisted together, side wire twist pitch 8~18mm. The invention of the steel complex aramid cord of high strength, light weight, increased cord stiffness, can withstand the higher fracture strength, and improve the adhesion between rubber and steel cord and the fatigue performance.

【技术实现步骤摘要】
钢丝芳纶复合帘线
本专利技术涉及钢帘线加工
，具体涉及一种钢丝芳纶复合帘线。
技术介绍
钢丝帘线作为子午线轮胎主要的骨架材料，有着强度高、耐冲击、抗变形、导热性能优等诸多优势，但钢帘线也存在着线密度大、耐疲劳和抗腐蚀性差等不足。芳纶作为一种新型的材料，由于其质量轻、强度高、耐腐蚀等优异的性能一经问世就得到了广泛的应用。很多轮胎厂都将其作为新型骨架材料的替代产品进行研究，但芳纶帘线也存在着不易于橡胶粘合、抗压缩能力差、刚度低以及轮胎操纵性不好的缺陷。复合帘线是一种将不同材质的长丝或纱线捻制在一起的新型帘线，可以发挥各自的优点，得到一种性能更为优越的橡胶骨架材料。复合帘线的概念在一些技术文献中已有相关的介绍，但是把两种不同材质的长丝捻在一起，还是有诸多的问题。钢丝芳纶复合帘线就存在两种材料断裂伸长率不一致的问题，虽然芳纶较其他纤维有高的模量和低的断裂伸长率，但同以高碳钢经过多道次拉拔的钢帘线单丝相比，仍然有较大的差异。除部分高模量芳纶外，大部分芳纶的断裂伸长率在2.5～4％，而湿拉后单丝的断裂伸长率在1.8～2.2％，这样形成的复合帘线会因钢丝和芳纶断裂伸长不同而发挥不了芳纶的强度本文档来自技高网...

【技术保护点】
钢丝芳纶复合帘线，包括芳纶芯和外层金属，其特征在于，所述芳纶芯包括多根捻合在一起的芳纶线，芳纶线的断裂伸长率为2.5~4%，所述外层金属包括多根面线钢丝，面线钢丝的断裂伸长率为2.5~4%，所述外层金属缠绕在芳纶芯的外层，两者捻合在一起，所述面线钢丝的捻距为8~18mm。

【技术特征摘要】
1.钢丝芳纶复合帘线，包括芳纶芯和外层金属，其特征在于，所述芳纶芯包括多根捻合在一起的芳纶线，芳纶线的断裂伸长率为2.5~4%，所述外层金属包括多根面线钢丝，面线钢丝的断裂伸长率为2.5~4%，所述外层金属缠绕在芳纶芯的外层，两者捻合在一起，所述面线钢丝的捻距为8~18mm。2.根据权利要求1所述的钢丝芳纶复合帘线，其特征在于，所述芳纶芯的密度为1000D~5000D。3.根据权利要求1所述的钢丝芳纶复合帘线，其特征在于，所述芳纶线的数量为1~3根，其规格为840D×2、1000D×2、1000D×3或1500D×2中的一种。4.根据权利要求3所述的钢丝芳纶复合帘线，其特征在于...