The invention belongs to the technical field of adhesive, conductive adhesive for a battery electrode, which comprises the following components: 2-5 parts by weight of carbon black, graphite powder 2-5, ethanol 50-100, Teflon 0.3-0.5, water 1-5; preparation, the PTFE is mixed with water and prepared into suspension emulsion, then stirring and slowly adding ethanol and continue to stir for 3-5 minutes until the PTFE dispersed in ethanol, then the mixed carbon black and graphite powder evenly and slowly add ethanol, stirring 10-15 minutes, heating to 90-100 DEG C, stirring until insulation water and ethanol evaporation drying time; the adhesive of the invention has good conductive ability, using active material quality less able to work with a large current can be used to add practical electrode in the battery, it is worth popularizing.
【技术实现步骤摘要】
一种电池电极专用导电黏合剂
本专利技术属于胶粘剂
，具体是一种电池电极专用导电黏合剂。
技术介绍
随着科学技术的不断发展，高科技产品的不断更新，人们对设备的体积要求越来越小，产品的待机时间要求越来越高，新型电池的开发研究成为目前最重要的课题之一，电池的开发研究离不开电极材料的研究，而电极材料的测试正是电池开发的重要步骤，这样就需要一种导电性能优良的电极材料胶粘剂，一般的胶粘剂导电性能差，电极测试时间长，测试效率低，并且毒性高，不论是在生产过程中还是在使用过程中，均会对劳动者的身体健康带来损害，因此，研发一种导电性能高，毒性低，且能够缩短测试时间、提高测试效率的新型导电黏合剂十分重要。
技术实现思路
本专利技术的目的就是针对目前普通的导电胶粘剂存在导电性能差，电极测试时间长，测试效率低，且原料毒性较大，在生产和使用过程中均会对劳动者造成身体损害的问题，而提供一种电池电极专用导电黏合剂。本专利技术的一种电池电极专用导电黏合剂,由下述重量份原料组成：炭黑2-5石墨粉2-5乙醇50-100聚四氟乙烯0.3-0.5水1-5；制备时，先将聚四氟乙烯与水混合配制成悬浊液，然后...
【技术保护点】
一种电池电极专用导电黏合剂,其特征在于由下述重量份原料组成：炭黑 2‑5 石墨粉 2‑5乙醇 50‑100 聚四氟乙烯 0.3‑0.5水 1‑5；制备时，先将聚四氟乙烯与水混合配制成悬浊液，然后在搅拌下缓慢加入乙醇中，继续搅拌3‑5分钟直至聚四氟乙烯均匀分散在乙醇中，然后将炭黑与石墨粉混合均匀后缓慢加入乙醇中，继续搅拌10‑15分钟，加热至90‑100℃，保温继续搅拌至水和乙醇蒸发干燥为止。
【技术特征摘要】
1.一种电池电极专用导电黏合剂,其特征在于由下述重量份原料组成：炭黑2-5石墨粉2-5乙醇50-100聚四氟乙烯0.3-0.5水1-5；制备时，先将聚四氟乙烯与水混合配制成悬浊液，然后在搅拌下...