一种三维有序大孔钴锰复合氧化物及其制备方法技术

本发明专利技术公布了一种三维有序大孔钴锰复合氧化物及其制备方法，三维有序大孔钴锰复合氧化物中金属钴和金属锰的摩尔比为1:2到2:1，具有三维有序大孔结构。制法为：六水合硝酸钴和硝酸锰溶液溶于含有甲醇和乙二醇的混合溶剂中，L‑赖氨酸溶于去离子水中柠檬酸调节溶液pH值为4.5‑5；将以上金属盐溶液和L‑赖氨酸混合后浸渍一定量聚甲基丙烯酸甲酯，抽滤，干燥后置于管式炉中，先在N

Three dimensional ordered macroporous cobalt manganese composite oxide and preparation method thereof

The invention discloses a three-dimensional ordered macroporous cobalt manganese oxide and its preparation method, molar ratio of metal cobalt and manganese metal composite three-dimensional ordered macroporous cobalt manganese oxides as 1:2 to 2:1, with a three-dimensional ordered macroporous structure. Method: Six hydrated cobalt nitrate and manganese nitrate solution in the mixed solvent containing methanol and ethylene glycol, L lysine dissolved in deionized water and citric acid solution was adjusted pH value of 4.5 5; the metal salt solution and L lysine after mixing a certain amount of poly methyl methacrylate impregnation. After filtration, drying in a tube furnace, the first in the N

【技术实现步骤摘要】
一种三维有序大孔钴锰复合氧化物及其制备方法
本专利技术涉及一种复合金属氧化物的制备领域，具体的说涉及一种三维有序大孔钴锰复合氧化物及其制备方法，属于材料制备领域。
技术介绍
钴锰复合氧化物因其在电学、磁学、光学及催化领域具有较好的应用前景，近年来受到广泛关注。如在电学领域，可表现出较好的电化学性能等；在催化领域，钴锰复合氧化物对挥发性有机物(VOCs)催化燃烧、一氧化碳(CO)氧化、一氧化氮(NO)氧化、选择催化还原(SCR)等反应均表现出较好的催化性能。三维有序大孔结构因其孔结构有序、规整，利于使得反应物分子通过，使得其具有较高的物理化学性能，因此在各种领域表现出优良的性能。尤其对于较大分子直径的VOCs气体，如苯系物、卤代芳烃等，较大的孔结构利于其穿过，因此可增加分子与材料本身的接触，增大反应概率，进而提高了反应性能。综合以上考虑，可将钴锰氧化物制备成三维有序大孔结构，并用于大分子气体参与的各种反应中。目前报道的方法中，常采用纳米复制法。简单归纳步骤如下：针对不同的金属氧化物，采用其盐溶液溶于一定的溶剂中，配制成前驱体溶液。后将该前驱体溶液浸渍具有规整排列的球的模板剂（如PS、P本文档来自技高网...

【技术保护点】
一种三维有序大孔钴锰复合氧化物，其特征在于：金属钴和金属锰的摩尔比为1:2到2:1，具有三维有序大孔结构的钴锰复合氧化物。

【技术特征摘要】
1.一种三维有序大孔钴锰复合氧化物，其特征在于：金属钴和金属锰的摩尔比为1:2到2:1，具有三维有序大孔结构的钴锰复合氧化物。2.根据权利要求1所述一种三维有序大孔钴锰复合氧化物的制备方法，其特征在于，所得钴锰复合氧化物的孔径大小为55-65nm。3.一种权利要求1或2所述三维有序大孔钴锰复合氧化物的制备方法，其特征在于，称取一定量的六水合硝酸钴（Co(NO3)2•6H2O）和质量分数为50%的硝酸锰溶液溶于含有甲醇和乙二醇的混合溶剂中，其中金属钴和金属锰的摩尔比为1:2到2:1，所用甲醇和乙二醇的比例为7:3，所得金属的总摩尔浓度为4.0mol/L；称取少量L...

【专利技术属性】
技术研发人员：何丹农，袁静，高振源，赵昆峰，金彩虹，
申请(专利权)人：上海纳米技术及应用国家工程研究中心有限公司，
类型：发明
国别省市：上海,31