一种微米级氧化铝粉体的制备装置制造方法及图纸
Device for preparing micron grade alumina powder
The invention discloses a device for preparing micron alumina powder, comprises a synthetic tower, distillation tower, high pressure wet crushing device, drying machine and high temperature sintering furnace, the pure aluminum, alcohol and catalyst are added according to the proportion in synthesis tower and heated to 80 to 120 DEG C, the synthesis of aluminum alcohol salt, and then sent to the aluminum alkoxide vacuum distillation tower is heated to 2mmHg 7mmHg after decompression, purified high pure aluminum pure salt, crushed then high purity aluminum alkoxide into high pressure wet crushing device, after drying machine drying and calcination furnace heated to 800 DEG C to 1500 DEG C after micron alumina powder. The alumina powder preparation device has the advantages of small size, low power consumption, etc..
【技术实现步骤摘要】
本专利技术涉及氧化铝粉体制造装置领域，具体涉及一种微米级氧化铝粉体的制备装置。
技术介绍
高纯氧化铝粉体做为一种高科技产品在国内外市场上具有广阔的前景，需求量都很大，并且逐年呈上升趋势。国内电子、人工晶体、化工、机械等行业的年需求约在300吨左右，供货渠道主要依靠进口；国外市场年需求量约在2000吨以上，每公斤价格高达120美元左右。氧化铝粉体的细度是该产品原料一个重要的指标，现有的粉体制备装置普遍存在结构复杂、能耗过高、细度不足等问题。
技术实现思路
针对上述问题，本专利技术提供一种微米级氧化铝粉体的制备装置。本专利技术的目的采用以下技术方案来实现：一种微米级氧化铝粉体的制备装置，包括依次相连的合成塔、减压蒸馏塔、湿式高压粉碎装置、烘干机和高温煅烧炉，将纯铝、醇和催化剂按比例加入合成塔中并加热到80℃～120℃，合成铝醇盐，然后将所得铝醇盐送至减压蒸馏塔中加热减压至2mmHg-7mmHg，经过提纯得到高纯铝纯盐，随后将高纯铝醇盐送入湿式高压粉碎装置中粉碎，经过烘干机烘干后由高温煅烧炉加热至800℃-1500℃，得到微米级氧化铝粉体。有益效果为：结构简单实用，得到的...
【技术保护点】
一种微米级氧化铝粉体的制备装置，其特征是，包括依次相连的合成塔、减压蒸馏塔、湿式高压粉碎装置、烘干机和高温煅烧炉，将纯铝、醇和催化剂按比例加入合成塔中并加热到80℃～120℃，合成铝醇盐，然后将所得铝醇盐送至减压蒸馏塔中加热减压至2mmHg‑7mmHg，经过提纯得到高纯铝纯盐，随后将高纯铝醇盐送入湿式高压粉碎装置中粉碎，经过烘干机烘干后由高温煅烧炉加热至800℃‑1500℃，得到微米级氧化铝粉体。
【技术特征摘要】
1.一种微米级氧化铝粉体的制备装置，其特征是，包括依次相连的合成塔、减压蒸馏塔、湿式高压粉碎装置、烘干机和高温煅烧炉，将纯铝、醇和催化剂按比例加入合成塔中并加热到80℃～120℃，合成铝醇盐，然后将所得铝醇盐送至减压蒸馏塔中加热减压至2mmHg-7mmHg，经过提纯得到高纯铝纯盐，随后将高纯...