Thermally assisted magnetic recording medium and magnetic storage device

The present invention provides a heat assisted magnetic recording medium, comprising: a substrate, a base layer formed on the substrate, and containing alloy with L10 structure as the main component of the magnetic layer, characterized in that at least 1 layers of the base layer containing MgO as a main component, and contains at least 1 a melting point of metal elements above 2000 DEG C. The thermally assisted magnetic recording medium has a uniform size and has a narrow field of switching field distribution (SFD), and a magnetic memory device including the thermally assisted magnetic recording medium exhibits a high signal-to-noise ratio.

【技术实现步骤摘要】

本专利技术涉及热辅助磁记录介质和使用该热辅助磁记录介质而成的磁存储装置。
技术介绍
通过对介质照射近场光等来使表面局部受热、降低介质的矫顽力、从而进行写入的热辅助记录方法，作为可以实现约lTbit/inch2或更高的面记录密度的新一代记录方式受到人们关注。在使用热辅助记录时，即使对于室温下矫顽力为几十个kOe的记录介质，目前也可以通过磁头的记录磁场轻松地进行写入。因此，记录层可以使用具有约106J/m3 107J/m3的高磁晶各向异性Ku的材料，可以在保持热稳定性的情况下使磁性粒子粒径变细微至6nm以下。作为这种高Ku材料，已知具有Li。型结晶结构的!^ePt合金(Ku :7X IO6J/ m3)、CoPt 合金(Ku :5X106J/m3)等。当磁性层中使用具有Lltl型结晶结构的!^ePt合金时，需要使该!^ePt合金采取 (001)取向。因此，优选在基底层中使用(100)取向的MgO。为了使MgO的(100)面与Ll0 Si^Pt合金的(001)面的晶格整合性良好，可以通过在(100)取向的MgO基底层上形成Li。 型i^ePt磁性层来使该磁性层呈(001)取向。另一方面本文档来自技高网...

【技术保护点】
１．一种热辅助磁记录介质，包含：基板，在该基板上形成的多个基底层，以及含有具有Ｌ１０结构的合金作为主成分的磁性层，其特征在于，该基底层中的至少１层含有ＭｇＯ作为主成分，并且含有至少１种熔点为２０００℃以上的金属元素。

【技术特征摘要】
...

【专利技术属性】
技术研发人员：神边哲也，桥本笃志，福岛隆之，
申请(专利权)人：昭和电工株式会社，
类型：发明