The invention relates to a method for preparing nano catalyst copper chromite and copper ferrite, which belongs to the field of nanometer catalyst preparation technology. The invention adopts sol-gel and vacuum freeze drying (VFD) method. Firstly, a soluble copper salt and a soluble chromate or iron salts formulated into a mixed solution, adding surfactant mixed evenly; then the precipitating agent added to the pH value of the system is 6.8 ~ 9.5 of the precipitation reaction, static aging, washing, at 70 to 95 DEG C water bath thawing glue 2 ~ 8h system it then sol; sol into the vacuum freeze dryer in freeze drying, prepared catalyst precursor gel; finally, the dry gel roasting to obtain copper chromite (CuCr: 2 O: 4) or copper ferrite (CuFe: 2 O: 4 nm) catalyst. The nanometer catalyst prepared by the invention has the advantages of high purity, small particle diameter, good dispersibility and high catalytic activity.
【技术实现步骤摘要】
本专利技术涉及一种制备CuCr204和CuFe204纳米催化剂的方法，属于催化剂制备领域。制备 方法涉及到溶胶_凝胶和真空冷冻干燥法。
技术介绍
纳米01&204和CuFeA是一类重要的催化剂，在许多催化反应中表现出良好的催化活性。 比如 一氧化碳催化加氢(YurevaTM，etal. Kine Catal，)、汽车尾气净化(Morgan W. J. Cat)、 食用油脂选择性催化加氢(Jakansson L E. J. Amer. oil Chem. Soc)。但是，制备方法限制了其 应用。传统的制备多采用共沉淀法或固相法，这些方法存在一些缺点粉体颗粒不均匀、硬 团聚严重、烧结温度较高、活性较低等。溶胶-凝胶和真空冷冻干燥法是一种制备纳米粉体的新技术，制备的纳米粉体优点包 括纯度高、粒径分布均匀、硬团聚少、晶形好且大小可控、副反应少，反应过程容易控制、 易于实现工业化等。针对传统方法制备亚铬酸铜和铁酸铜催化剂存在硬团聚严重、颗粒不均匀、活性低等缺 点，本专利技术采用溶胶-凝胶和真空冷冻干燥法制备出了纯度高、粒径小、分散性好、硬团聚 少、催化活性高的具...
【技术保护点】
一种制备纳米催化剂ＣｕＣｒ↓［２］Ｏ↓［４］的方法，其特征在于该方法按如下步骤进行： （１）溶胶的制备： ａ．配制摩尔比为１∶２的可溶性铜盐与可溶性铬盐的混合溶液，其中铜盐浓度为０．１～０．５ｍｏｌ／Ｌ；加入质量百分数为０．１％～５％的表面活性剂，搅拌均匀； ｂ．将沉淀剂水溶液以２０～１８０ｍｌ／ｈ速率加到混合溶液中，至体系ｐＨ为６．８～９．５，静置老化，离心或抽虑洗涤，得到沉淀物； ｃ．向所得沉淀物中加入质量百分比为８％～４０％去离子水，于７０～９５℃的恒温水浴中胶融２～８ｈ，得到溶胶； （２）凝胶的制备： 将溶胶用真空冷冻干燥法在－４５～－８０℃，１～３０Ｐａ的真空度下...
【技术特征摘要】
【专利技术属性】
技术研发人员：苏涛，张平，王来军，陈崧哲，王志超，姚桃英，徐景明，
申请(专利权)人：清华大学，
类型：发明
国别省市：11[中国|北京]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。