本发明专利技术涉及一种不定岛超细纤维绒面革的耐刮处理方法，是以聚酰胺（ＰＡ６）为“岛”，以低密度聚乙烯（ＰＥ）为“海”，同时加入微量离子聚合物，利用单螺杆共混法纺得的超细纤维。经过针刺无纺布，含浸ＰＵ树脂、甲苯减量、扩幅干燥、片皮和磨皮等处理而制得超细纤维绒面革；在生产流程中，由于离子化合物的作用，超细纤维“岛”与“岛”之间有一定量的交联，防止以绒面革为材料做成手套、鞋、服装和箱包等产品时，绒面革中纤维的脱落，从而大大提高绒面革的耐刮性。

Scratch resistant treatment method of indefinite island superfine fiber suede leather

The invention relates to a sea island ultrafine fiber suede scratch processing method, is based on polyamide (PA6) as the \island\, with low density polyethylene (PE) as the \sea\, while adding trace ion polymer superfine fiber by single screw blending method of spinning. After the acupuncture non-woven fabric, impregnated with PU resin, toluene reduction, expanding dry, skin and skin grinding processing and preparation of superfine fiber suede; in the production process, because the function of ionic compound, a certain amount of crosslinking between superfine fiber \island\ and \island\, to prevent the suede material the product made of gloves, shoes, clothing and bags etc., shedding suede fibre, thus greatly improving the suede scratch resistance.

【技术实现步骤摘要】

本专利技术涉及一种不定岛超细纤维绒面革，尤其涉及该不定岛超细纤维 绒面革的耐刮处理方法。
技术介绍
绒面革的耐刮性是超细纤维合成革使用过程中的一个重要指标，现在 国内绒面革的纤维采用不定岛的单螺杆挤压机法纺丝(参见张大省、王 锐.超细纤维生产技术及应用)。该产品存在一个较大的局限性纤维内岛 的轴向不连续且很不均匀，在后续的产成品中纤维很容易脱落，书写性较 差。
技术实现思路
本专利技术需要解决的技术问题是提供了一种不定岛超细纤维绒面革的耐刮处理方法，旨在解决上述的问题。为了解决上述技术问题，本专利技术是通过以下步骤实现的 采用双组分共混熔融纺丝得到海岛纤维，其中以尼龙(PA6)为"岛"，以低密度聚乙烯为"海"，同时加入微量离子聚合物；其中尼龙(PA6):聚乙烯(pu):离子聚合物的重量比为60 40%: 40 60%: 0.1 0.6%; 将上述海岛型超细纤维经开松、梳理、铺网和针刺而制得无纺布； 将无纺布烫平热定型后含浸聚氨脂(PU)树脂，然后采用二甲基甲酰胺(DMF)水溶液使聚氨脂树脂凝固，再用温水将二甲基甲酰胺置换出来; 利用甲苯溶液将海岛纤维中的低密度聚乙烯萃取出来，即将"本文档来自技高网...

【技术保护点】
一种不定岛超细纤维绒面革的耐刮处理方法，是通过以下步骤实现的：　（１）、采用双组分共混熔融纺丝得到海岛纤维，其中以尼龙为“岛”，以低密度聚乙烯为“海”，同时加入微量离子聚合物；其中尼龙∶聚乙烯∶离子聚合物的重量比为６０～４０％∶４０～ ６０％∶０．１～０．６％；　（２）、将上述海岛型超细纤维经开松、梳理、铺网和针刺而制得无纺布；　（３）、将无纺布烫平热定型后含浸聚氨脂树脂，然后采用二甲基甲酰胺水溶液使聚氨脂树脂凝固，再用温水将二甲基甲酰胺置换出来；　（４ ）、利用甲苯溶液将海岛纤维中的低密度聚乙烯萃取出来，即将“海”抽出，使基布中仅含有尼龙、改性离子...