The invention discloses a sea island ultrafine fiber suede wool dyeing method, which comprises the following steps: (1) the sea island ultrafine fiber suede leather and wool reactive dyes in the dye bath, using acetic acid pH was adjusted to 3~7, from 0.3 to 2 DEG /min to room temperature rate of heating to 90~120 DEG C the insulation of 10 ~ 70min, and then to 1~3 DEG /min to 20~60 DEG C; (2) adjusting pH dye bath, solid color, can be dyed the sea island ultrafine fiber suede. The dyeing depth, color uniformity and dry rubbing fastness of the invention are basically the same. The wet rubbing fastness is about 1~2 grade. The dyeing wastewater contains no heavy metal ions and is environmentally friendly. The invention solves the problem of low wet rubbing fastness and large pollution of dyeing wastewater in the conventional dyeing of the ultra fine fiber suede in the existing technology.
【技术实现步骤摘要】
定岛超细纤维绒面革毛用活性染料染色方法
本专利技术涉及定岛超细纤维绒面革毛的染色方法。
技术介绍
超细纤维合成革是继PVC、PU之后的第三代人造皮革，它是采用与天然皮革中定岛胶原纤维的结构和性能相似的锦纶6超细纤维，制成具有三维网状结构的高密度无纺布，再填充性能优异具有开式微孔结构的聚氨酯，经后加工处理而成的。这种合成革具有定岛超细胶原纤维天然革所固有的吸湿性。因而，无论是从内部微观结构，还是外观质感、物理特性和穿着舒适性等方面，都能够与高级天然皮革相媲美。此外，超细纤维合成革在耐化学性、质量均一性、生产加工适应性以及防水防霉变性等方面都优于天然皮革，用以制作箱包、服装、鞋以及汽车内饰等，具有广阔的发展前景。超细纤维合成革由超细锦纶6纤维和聚氨酯两部分组成。锦纶6为聚酰胺结构，分子结构中含有端胺基，可由酸性染料、中性染料和毛用活性染料染色。但是超细锦纶6纤维比普通纤维细的多，比表面积大，所以在染色中存在一系列问题，如上染速率过快、显色性差以及染色牢度差等。聚氨酯的主要化学组成是聚氨基甲酸酯，它是由软链段和硬链段组成的嵌段共聚物。采用酸性染料染色，产品的染色牢度差，...
【技术保护点】
定岛超细纤维绒面革毛用活性染料染色方法，其特征在于，包括如下步骤：(1)将定岛超细纤维绒面革和毛用活性染料置于染浴中，采用醋酸调节pH为3～7，从室温以0.3～2℃/min速度升温至90～120℃，保温10～70min，然后以1～3℃/min降至20～60℃；(2)调节染浴的pH，固色，即可获得染色的定岛超细纤维绒面革。
【技术特征摘要】
1.定岛超细纤维绒面革毛用活性染料染色方法，其特征在于，包括如下步骤：(1)将定岛超细纤维绒面革和毛用活性染料置于染浴中，采用醋酸调节pH为3～7，从室温以0.3～2℃/min速度升温至90～120℃，保温10～70min，然后以1～3℃/min降至20～60℃；(2)调节染浴的pH，固色，即可获得染色的定岛超细纤维...
【专利技术属性】
技术研发人员：胡忠杰，韩芹，张其斌，孙向浩，
申请(专利权)人：上海华峰超纤材料股份有限公司，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。