一种C80泵送混凝土及其制备方法技术

本发明专利技术涉及一种混凝土，特别涉及Ｃ８０泵送混凝土；本发明专利技术还涉及其制备方法。一种Ｃ８０泵送混凝土，其特征在于，由以下重量比的原料制备而成：水，０．２６；复合胶凝材料，１．００；砂，１．２１；碎石，１．７２；外加剂，占原料总重量的２．３２％。该Ｃ８０泵送混凝土的制备方法是，将原料混合在搅拌机中搅拌，搅拌机的电机电流为６０～７０Ａ，搅拌时间为１２０～１８０ｓ，投料顺序如下：１）先投入碎石和６０％～８０％的砂，搅拌１０ｓ；２）然后投入复合凝胶材料，搅拌２０ｓ；在第１０ｓ时开始加入７０～８０％的水，水中投入外加剂；３）然后投入剩余的砂，搅拌２０ｓ；４）然后加入剩余的水，搅拌７０ｓ～１３０ｓ；５）出料。

C80 pumping concrete and preparation method thereof

The invention relates to a concrete, in particular to a C80 pumping concrete. A C80 pump concrete, which is characterized by the following weight ratio is prepared with water: 0.26; 1; composite cementitious materials, sand, gravel, 1.21; 1.72; additives, raw materials accounted for the total weight of 2.32%. The preparation method of C80 pump concrete is mixed in a stirrer, mixer motor current is 60 ~ 70A, the stirring time is 120 ~ 180s, the feeding order is as follows: 1) first put 60% to 80% of the gravel and sand mixing, 10s; 2) and then into composite gel material, mixing 20s; at 10s began adding 70 ~ 80% of the water, water input additive; 3) and then put the remaining sand mixing, 20s; 4) and then add the remaining water, stirring 70s ~ 130s; 5) material.

【技术实现步骤摘要】

本专利技术涉及一种混凝土，特别涉及C80泵送混凝土；本专利技术还涉及其制备方法。
技术介绍
高强度混凝土(＞C50)的出现是20世纪70年代以后的事，随着科学技术的迅速发展和混凝土技术的不断进步，世界各国使用的混凝土平均强度不断提高。发展高强度等级的混凝土，在减轻结构自重、满足强度、节约材料和节省资金等方面都有良好的技术经济效果。因此，根据实际运用中对C80混凝土的要求，在现有设备条件下，针对高性能、高强度混凝土的材料选择、配比确定和现场试验进行了探讨和研究。尤其在现有单卧轴搅拌设备前提下，针对C80混凝土的特性，着力对制备搅拌工艺流程的改良进行实践研究。通过实验来最终确定与生产相适应的制备搅拌工艺流程。
技术实现思路
本专利技术所要解决的技术问题的第一方面在于提出一种C80泵送混凝土。 本专利技术通过以下技术方案解决上述技术问题 一种C80泵送混凝土，其特征在于，由以下重量比的原料制备而成 水0.26 复合胶凝材料 1.00 砂1.21 碎石1.72 外加剂 占原料总重量的2.32％。 所述复合胶凝材料由水泥、粉媒灰、矿粉混合而成，其重量本文档来自技高网...

【技术保护点】
一种Ｃ８０泵送混凝土，其特征在于，由以下重量比的原料制备而成：　水　０．２６　复合胶凝材料　１．００　砂　１．２１　碎石　１．７２　外加剂　占原料总重量的２．３２％。

【技术特征摘要】

【专利技术属性】
技术研发人员：吴德龙，张皓，魏劼，吴慧华，陈尧亮，董毅君，吴勤，张海峰，
申请(专利权)人：上海建工材料工程有限公司，
类型：发明
国别省市：31[中国|上海]